Supercritical CO2 Foaming of Radiation Cross-Linked Isotactic Polypropylene in the Presence of TAIC
文献类型：期刊论文
| 作者 | Yang, CG; Wang, MH; Zhang, MX; Li, XH; Wang, HL; Xing, Z; Ye, LF; Wu, GZ |
| 刊名 | MOLECULES
 |
| 出版日期 | 2016 |
| 卷号 | 21期号:12页码:- |
| 关键词 | polypropylene TAIC radiation cross-linking supercritical carbon dioxide foaming |
| ISSN号 | 1420-3049 |
| 通讯作者 | Wu, GZ (reprint author), Chinese Acad Sci, Shanghai Inst Appl Phys, Jialuo Rd 2019, Shanghai 201800, Peoples R China. ; Wu, GZ (reprint author), ShanghaiTech Univ, Sch Phys Sci & Technol, Haike Rd 100, Shanghai 201210, Peoples R China. |
| 英文摘要 | Since the maximum foaming temperature window is only about 4 degrees C for supercritical CO2 (scCO(2)) foaming of pristine polypropylene, it is important to raise the melt strength of polypropylene in order to more easily achieve scCO(2) foaming. In this work, radiation cross-linked isotactic polypropylene, assisted by the addition of a polyfunctional monomer (triallylisocyanurate, TAIC), was employed in the scCO(2) foaming process in order to understand the benefits of radiation cross-linking. Due to significantly enhanced melt strength and the decreased degree of crystallinity caused by cross-linking, the scCO(2) foaming behavior of polypropylene was dramatically changed. The cell size distribution, cell diameter, cell density, volume expansion ratio, and foaming rate of radiation-cross-linked polypropylene under different foaming conditions were analyzed and compared. It was found that radiation cross-linking favors the foamability and formation of well-defined cell structures. The optimal absorbed dose with the addition of 2 wt % TAIC was 30 kGy. Additionally, the foaming temperature window was expanded to about 8 degrees C, making the handling of scCO(2) foaming of isotactic polypropylene much easier. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000392140100054 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/26639]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Yang, CG,Wang, MH,Zhang, MX,et al. Supercritical CO2 Foaming of Radiation Cross-Linked Isotactic Polypropylene in the Presence of TAIC[J]. MOLECULES,2016,21(12):-. |
| APA | Yang, CG.,Wang, MH.,Zhang, MX.,Li, XH.,Wang, HL.,...&Wu, GZ.(2016).Supercritical CO2 Foaming of Radiation Cross-Linked Isotactic Polypropylene in the Presence of TAIC.MOLECULES,21(12),-. |
| MLA | Yang, CG,et al."Supercritical CO2 Foaming of Radiation Cross-Linked Isotactic Polypropylene in the Presence of TAIC".MOLECULES 21.12(2016):-. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。