Nitrogen-doped hollow mesoporous carbon spheres as a highly active and stable metal-free electrocatalyst for oxygen reduction
文献类型：期刊论文
| 作者 | Zhou, Tingsheng1,2; Zhou, Yao1; Ma, Ruguang1; Zhou, Zhenzhen1; Liu, Guanghui1; Liu, Qian1,3; Zhu, Yufang2; Wang, Jiacheng1,3 |
| 刊名 | CARBON
 |
| 出版日期 | 2017-04-01 |
| 卷号 | 114页码:177-186 |
| 英文摘要 | Nitrogen-doped hollow mesoporous carbon spheres (NHCSs) were successfully prepared via a simple, scalable hydrothermal method, followed by thermal treatment at 650 degrees C in ammonia atmosphere and subsequent high temperature annealing at 800-1000 degrees C in nitrogen, respectively. The resulting NHCSs with a particle diameter of 150 nm and a shell thickness of 20-25 nm have high specific surface areas (738-820 m(2) g(-1)), large pore volume (0.50-0.56 cm3 ri), bimodal pores system (3.9 and 51.6 nm) and adjustable N-doping levels (3.6-7.8 at.%) depending on the pyrolysis temperature. The unique structure of hollow spheres for NHCSs with uniform mesopores throughout the shells can both promote fast mass transfer and provide inner and outer surfaces with high density of N-related active sites, thus improving the reaction kinetics. The NHCS-1000 (annealed at 1000 degrees C) exhibited not only comparable ORR activity with a direct four-electron reaction pathway in terms of onset and half-wave potentials, and limiting current densities, but superior long-term durability and methanol-tolerance to commercial Pt/C catalyst, because it has the highest relative content of graphitic-Nand pyridinic-N groups, indicating their crucial roles in ORR. The NHCS-1000 with excellent ORR performance is of potential to replace Pt/C catalyst for ORR in practical applications. (C) 2016 Elsevier Ltd. All rights reserved. |
| WOS标题词 | Science & Technology ; Physical Sciences ; Technology |
| 类目[WOS] | Chemistry, Physical ; Materials Science, Multidisciplinary |
| 研究领域[WOS] | Chemistry ; Materials Science |
| 关键词[WOS] | CATALYST ; EFFICIENT ; GRAPHENE ; PERFORMANCE ; LAYERS |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000393249600021 |
| 源URL | [http://ir.sic.ac.cn/handle/331005/23486]  |
| 专题 | 上海硅酸盐研究所_高性能陶瓷和超微结构国家重点实验室_期刊论文 |
| 作者单位 | 1.Chinese Acad Sci, Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine, 1295 Dingxi Rd, Shanghai 200050, Peoples R China 2.Univ Shanghai Sci & Technol, Sch Mat Sci & Engn, 516 Jungong Rd, Shanghai 200093, Peoples R China 3.Shanghai Inst Mat Genome, Shanghai, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhou, Tingsheng,Zhou, Yao,Ma, Ruguang,et al. Nitrogen-doped hollow mesoporous carbon spheres as a highly active and stable metal-free electrocatalyst for oxygen reduction[J]. CARBON,2017,114:177-186. |
| APA | Zhou, Tingsheng.,Zhou, Yao.,Ma, Ruguang.,Zhou, Zhenzhen.,Liu, Guanghui.,...&Wang, Jiacheng.(2017).Nitrogen-doped hollow mesoporous carbon spheres as a highly active and stable metal-free electrocatalyst for oxygen reduction.CARBON,114,177-186. |
| MLA | Zhou, Tingsheng,et al."Nitrogen-doped hollow mesoporous carbon spheres as a highly active and stable metal-free electrocatalyst for oxygen reduction".CARBON 114(2017):177-186. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。