Chemical process and solid solution formation in reactive hot pressed ZrB2-SiC ceramics doped with W
文献类型：期刊论文
| 作者 | Liu, H. -L.1,2; Ma, H. -B.1,2; Liu, J. -X.1; Liu, H. -T.1; Zhang, G. -J.1 |
| 刊名 | ADVANCES IN APPLIED CERAMICS
 |
| 出版日期 | 2017 |
| 卷号 | 116期号:2页码:118-122 |
| 关键词 | Zrb(2)-SiC tungsten boride solid solution reactive hot pressing microstructures |
| 英文摘要 | ZrB2-SiC doped with W was prepared from a mixture of Zr, Si, B4C and W via reactive hot pressing. The fully dense ZrB2-SiC-WB-ZrC ceramic was obtained at 1900 degrees C for 60 min under 30MPa in an argon atmosphere. Reaction path and solid solution characteristics of the starting powders were studied through a series of pressureless heat treatment at temperatures between 700 and 1500 degrees C. The solid solution phases of (Zr, W)B-2, (W, Zr)B and (Zr, W)C were formed directly by reactions between the precursors. Homogeneous distribution of solute atoms in solution and the solid solubilities were also studied. |
| WOS标题词 | Science & Technology ; Technology |
| 类目[WOS] | Materials Science, Ceramics |
| 研究领域[WOS] | Materials Science |
| 关键词[WOS] | IN-SITU SYNTHESIS ; HIGH-TEMPERATURE CERAMICS ; MECHANICAL-PROPERTIES ; COMPOSITES ; DENSIFICATION ; MICROSTRUCTURE |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000395242500008 |
| 源URL | [http://ir.sic.ac.cn/handle/331005/23574]  |
| 专题 | 上海硅酸盐研究所_高性能陶瓷和超微结构国家重点实验室_期刊论文 |
| 作者单位 | 1.Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine, Shanghai 200050, Peoples R China 2.Univ Chinese Acad Sci, Beijing, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, H. -L.,Ma, H. -B.,Liu, J. -X.,et al. Chemical process and solid solution formation in reactive hot pressed ZrB2-SiC ceramics doped with W[J]. ADVANCES IN APPLIED CERAMICS,2017,116(2):118-122. |
| APA | Liu, H. -L.,Ma, H. -B.,Liu, J. -X.,Liu, H. -T.,&Zhang, G. -J..(2017).Chemical process and solid solution formation in reactive hot pressed ZrB2-SiC ceramics doped with W.ADVANCES IN APPLIED CERAMICS,116(2),118-122. |
| MLA | Liu, H. -L.,et al."Chemical process and solid solution formation in reactive hot pressed ZrB2-SiC ceramics doped with W".ADVANCES IN APPLIED CERAMICS 116.2(2017):118-122. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。