TeO2-Nb2O5-YF3玻璃系统的形成区及性质研究
文献类型：期刊论文
| 作者 | 吴家禄 ; 张军杰 ; 汪国年 ; 胡丽丽 ; 姜中宏 |
| 刊名 | 光学学报
 |
| 出版日期 | 2007 |
| 卷号 | 27期号:8页码:1449 |
| 关键词 | 光学材料 碲酸盐玻璃 红外 [OH]吸收 optical materials tellurite glass infrared [OH] absorption |
| ISSN号 | 0253-2239 |
| 其他题名 | Formation and Properties of Glass in Ternary TeO2-Nb2O5-YF3System |
| 中文摘要 | 制备了一种新型的氧卤碲酸盐玻璃：TeO2-Nb2O5-YF3,给出并研究了TeO2-Nb2O5-YF3三元系统的玻璃形成范围。测试了玻璃的密度、折射率、差热(DTA)、拉曼光谱、红外透射光谱以及紫外吸收光谱,通过光谱分析研究了组分含量的变化对玻璃结构及红外透射特性的影响。实验结果表明,TeO2-Nb2O5-YF3玻璃系统具有优良的成玻璃性能和热稳定性等特性,而且在2.8～3.3 μm区域内无明显的[OH]基团吸收,在中红外3～5 μm区域具有优良透射性能,因此在中红外透射方面具有潜在应用价值。; The ternary TeO2-Nb2O5-YF3 glass was synthesized and the formation range of TeO2-Nb2O5-YF3 glass system was investigated. The density, refractive index, differential thermal property (DTA), Raman spectra, UV absorption spectra and infrared transmission spectra of the samples were tested. The effects of composition content change on the structure and infrared transmission properties of glasses were investigated by spectra analysis. The results show that the glass forming ability and thermal stability of the ternary TeO2-Nb2O5-YF3 glass are good. The presented oxyhalide tellurite glass exhibits a high transmissivity (80%) in the mid-infrared regions (3～5 μm). There is no evident [OH] absorption bands in the range of 2.8～3.3 μm. |
| 学科主题 | 光学材料;光学玻璃 |
| 分类号 | TB321;TB34 |
| 收录类别 | ei |
| 语种 | 中文 |
| 公开日期 | 2009-09-24 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/4989]  |
| 专题 | 上海光学精密机械研究所_高功率激光单元技术研发中心 |
| 推荐引用方式 GB/T 7714 | 吴家禄,张军杰,汪国年,等. TeO2-Nb2O5-YF3玻璃系统的形成区及性质研究[J]. 光学学报,2007,27(8):1449, 1454. |
| APA | 吴家禄,张军杰,汪国年,胡丽丽,&姜中宏.(2007).TeO2-Nb2O5-YF3玻璃系统的形成区及性质研究.光学学报,27(8),1449. |
| MLA | 吴家禄,et al."TeO2-Nb2O5-YF3玻璃系统的形成区及性质研究".光学学报 27.8(2007):1449. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。