焙烧程序对一步合成Cu-SSZ-13催化剂NH_3-SCR性能的影响
文献类型：期刊论文
| 作者 | 谢利娟; 刘福东; 石晓燕; 贺泓 |
| 刊名 | 化工进展
 |
| 出版日期 | 2016 |
| 卷号 | 35期号:8页码:2464-2468 |
| 关键词 | 选择催化还原 分子筛 催化 焙烧程序 |
| 其他题名 | Influence of calcination procedure on the one-pot synthesized Cu-SSZ-13 catalysts and their performance in NH_3-SCR |
| 中文摘要 | 焙烧程序影响一步合成法制备Cu-SSZ-13催化剂中Cu物种的种类及分布,是影响催化剂在NH_3选择性催化还原(NH_3-SCR)氮氧化物反应中催化性能的重要因素。为研究焙烧程序对该方法制备Cu-SSZ-13催化剂性能的影响,采用不同的焙烧温度及升温速率制备Cu-SSZ-13催化剂,并考察各催化剂的催化活性、水热稳定性及活性物种形态。结果表明焙烧温度不改变催化剂的晶型结构,但影响催化剂的活性物种形态及稳定性。当焙烧温度为600℃时,催化剂中Cu物种全部为孤立的Cu~(2+),并具有极高的稳定性,催化剂具有最佳的活性及水热稳定性。固定焙烧温度为600℃,随升温速率的提高,催化剂活性及水热稳定性表现出下降趋势,考虑经济成本,最佳的升温速率应为1℃/min。因此,以1℃/min的升温速率升至600℃焙烧6h是一步合成法制备Cu-SSZ-13催化剂的最佳焙烧程序,所得催化剂具备优异的NH_3-SCR活性和水热稳定性。 |
| 英文摘要 | The calcination procedures affected the state and the distribution of Cu species in the one-pot synthesized Cu-SSZ-13,which then influenced their catalytic performance greatly. In order to investigate the effect of calcination procedure on the Cu-SSZ-13 in the selective catalytic reduction of NO_x by ammonia (NH_3-SCR),we prepared the catalysts with different temperatures and ramp rates. The catalytic activity and hydrothermal stability and state of active species of the catalysts were tested. The calcination temperature did not change the structure of the catalyst,but affected the state and the stability of the active species. When the temperature was set at 600℃,all Cu species in the catalyst were isolated Cu~(2+) with excellent stability,and the catalyst showed the best catalytic performance and hydrothermal stability. When the temperature was fixed at 600℃,the activity and hydrothermal stability of the catalysts decreased with the increase of ramp rate. Considering the cost,we had better set the ramp rate as 1℃/min. Thus,the optimal procedure was to calcine sample at 600℃ for 6h with a ramp rate of 1℃/min,and the catalyst showed the best NH_3-SCR activity and the highest hydrothermal stability. |
| 收录类别 | CSCD |
| CSCD记录号 | CSCD:5765396 |
| 源URL | [http://ir.rcees.ac.cn/handle/311016/36589]  |
| 专题 | 生态环境研究中心_大气污染控制中心 |
| 推荐引用方式 GB/T 7714 | 谢利娟,刘福东,石晓燕,等. 焙烧程序对一步合成Cu-SSZ-13催化剂NH_3-SCR性能的影响[J]. 化工进展,2016,35(8):2464-2468. |
| APA | 谢利娟,刘福东,石晓燕,&贺泓.(2016).焙烧程序对一步合成Cu-SSZ-13催化剂NH_3-SCR性能的影响.化工进展,35(8),2464-2468. |
| MLA | 谢利娟,et al."焙烧程序对一步合成Cu-SSZ-13催化剂NH_3-SCR性能的影响".化工进展 35.8(2016):2464-2468. |
入库方式： OAI收割
来源：生态环境研究中心
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。