gamma-LiAlO2 single crystal grown by Czochralski technique and modified by vapor transport equilibration (VTE) technique
文献类型：期刊论文
| 作者 | Zou J(邹军) ; Zhang LH(张连翰) ; Xu J(徐军) ; Zhou SM(周圣明) |
| 刊名 | j. mater. sci. technol.
 |
| 出版日期 | 2006 |
| 卷号 | 22期号:4页码:491 |
| 关键词 | gamma-LiAlO2 crystal vapor transport equilibration (VTE) technique Czochralski technique |
| ISSN号 | 1005-0302 |
| 中文摘要 | large-sized (similar to 2 inch, 50.8 mm) gamma-ua102 single crystal has been grown by conventional czochralski (cz) method, but the crystal ha's a milky, dendriform center. the samples taken from transparent and milky parts were ground and examined by x-ray diffraction. all diffraction peaks could be indexed in gamma-lialo2. the crystal quality was characterized by x-ray rocking curve. the full-width at half-maximum (fwhm) values are 116.9 and 132.0 arcsec for transparent and milky parts, respectively. the vapor transport equilibrium (vte) technique was introduced to modify the crystal quality. after 1000 degrees c/48 h, 1100 degrees c/48 h, 1200 degrees c/48 h vte processes, the fwhm values dropped to 44.2 and 55.2 arcsec for transparent and milky part, respectively. the optical transmission of transparent part was greatly enhanced from 85% to 90%, and transmission of milky part from 75% to 80% in the range of 190 similar to 1900 nm at room temperature. when the vte temperature was raised to 1300 degrees c, the sample cracked and fwhm values of transparent and milky parts were increased to 55.2 and 80.9 arcsec, respectively. by combining cz technique with vte technique, large-sized and high quality gamma-lialo2 crystal can be obtained. |
| 学科主题 | 光学材料;晶体 |
| 收录类别 | EI |
| 语种 | 英语 |
| WOS记录号 | WOS:000239637200014 |
| 公开日期 | 2009-09-24 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/5619]  |
| 专题 | 上海光学精密机械研究所_激光与光电子功能材料研发中心 |
| 推荐引用方式 GB/T 7714 | Zou J,Zhang LH,Xu J,et al. gamma-LiAlO2 single crystal grown by Czochralski technique and modified by vapor transport equilibration (VTE) technique[J]. j. mater. sci. technol.,2006,22(4):491, 494. |
| APA | 邹军,张连翰,徐军,&周圣明.(2006).gamma-LiAlO2 single crystal grown by Czochralski technique and modified by vapor transport equilibration (VTE) technique.j. mater. sci. technol.,22(4),491. |
| MLA | 邹军,et al."gamma-LiAlO2 single crystal grown by Czochralski technique and modified by vapor transport equilibration (VTE) technique".j. mater. sci. technol. 22.4(2006):491. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。