Hydrothermal growth and characterization of ZnO crystals
文献类型：期刊论文
| 作者 | Zhang Chang-Long ; Zhou Wei-Ning ; Hang Ying ; L ; Zhi ; Hou Hang-De ; Zuo Yan-Bin ; Qin Shi-Jie ; Lu Fu-Hua ; Gu Shu-Lin |
| 刊名 | j. cryst. growth
 |
| 出版日期 | 2008 |
| 卷号 | 310期号:7～9页码:1819 |
| 关键词 | characterization substrates hydrothermal crystal growth oxides zinc compounds semiconducting II-V materials |
| ISSN号 | 0022-0248 |
| 中文摘要 | zno crystals with dimensions of 30 x 38 x 8 turn 3 have been grown by the hydrothermal method using a mixed solution of koh, lioh and h2o2. the growing rates for +c(0001) and -c(000 (1) over bar) were 0.17 and 0.09 mm/day, respectively. the crystal color was very light green for +c sector and dark brown for -c sector. for the +c sector, the resistivity at room temperature was 80 0 cm, the carrier concentration was about 10(4)/cm(3), and the mobility was about 100 cm(2)/vs. the full-width at half-maximum (fwhm) of double axis x-ray rocking curve for the polished zn face cut from +c sector was 45 arcsec. the photoluminescence (pl) spectrum and the absorption spectrum of +c part of the crystals at room temperature were also reported and discussed in this paper. (c) 2008 elsevier b.v. all rights reserved. |
| 学科主题 | 光学材料;晶体 |
| 收录类别 | EI |
| 语种 | 英语 |
| WOS记录号 | WOS:000255843200095 |
| 公开日期 | 2009-09-24 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/6083]  |
| 专题 | 上海光学精密机械研究所_激光与光电子功能材料研发中心 |
| 推荐引用方式 GB/T 7714 | Zhang Chang-Long,Zhou Wei-Ning,Hang Ying,et al. Hydrothermal growth and characterization of ZnO crystals[J]. j. cryst. growth,2008,310(7～9):1819, 1822. |
| APA | Zhang Chang-Long.,Zhou Wei-Ning.,Hang Ying.,L.,Zhi.,...&Gu Shu-Lin.(2008).Hydrothermal growth and characterization of ZnO crystals.j. cryst. growth,310(7～9),1819. |
| MLA | Zhang Chang-Long,et al."Hydrothermal growth and characterization of ZnO crystals".j. cryst. growth 310.7～9(2008):1819. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。