Study of a high power density sodium polysulfide/bromine energy storage cell
文献类型：期刊论文
| 作者 | Ge, SH; Yi, BL; Zhang, HM |
| 刊名 | journal of applied electrochemistry
 |
| 出版日期 | 2004-02-01 |
| 卷号 | 34期号:2页码:181-185 |
| 关键词 | bromine cation exchange membrane energy storage nickel catalyst sodium polysulfide |
| 产权排序 | 1;1 |
| 英文摘要 | nickel catalyst supported on carbon was made by reduction of nickelous nitrate with hydrogen at high temperature. ni/ c catalyst characterization was carried out by xrd. it was found that the crystal phase of nis and nis2 appeared in the impregnated catalyst. ni/ c and pt/ c catalysts gave high performance as the positive and negative electrodes of a sodium polysulfide/ bromine energy storage cell, respectively. the overpotentials of the positive and negative electrodes were investigated. the effect of the electrocatalyst loading and operating temperature on the charge and discharge performance of the cell was investigated. a power density of up to 0.64 w cm(-2) ( v = 1.07 v) was obtained in this energy storage cell. a cell potential efficiency of up to 88.2% was obtained when both charge and discharge current densities were 0.1 a cm(-2). |
| WOS标题词 | science & technology ; physical sciences |
| 类目[WOS] | electrochemistry |
| 研究领域[WOS] | electrochemistry |
| 关键词[WOS] | electrodes ; performance ; platinum ; kinetics |
| 收录类别 | SCI |
| 原文出处 | true |
| 语种 | 英语 |
| WOS记录号 | WOS:000187517700008 |
| 公开日期 | 2010-11-30 |
| 源URL | [http://159.226.238.44/handle/321008/82619]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | Chinese Acad Sci, Dalian Inst Chem Phys, Fuel Cell R&D Ctr, Dalian 116023, Peoples R China |
| 推荐引用方式 GB/T 7714 | Ge, SH,Yi, BL,Zhang, HM. Study of a high power density sodium polysulfide/bromine energy storage cell[J]. journal of applied electrochemistry,2004,34(2):181-185. |
| APA | Ge, SH,Yi, BL,&Zhang, HM.(2004).Study of a high power density sodium polysulfide/bromine energy storage cell.journal of applied electrochemistry,34(2),181-185. |
| MLA | Ge, SH,et al."Study of a high power density sodium polysulfide/bromine energy storage cell".journal of applied electrochemistry 34.2(2004):181-185. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。