Corrosion Behavior of Q235 Carbon Steel in Presence of H2S Producing Bacillus sp and a Consortium of Microbes Isolated from Inner Rust Layer
文献类型：期刊论文
| 作者 | Zhang, Meixia1,2 ; Liu, Haixia1,2; Karn, Santosh Kr1; Duan, Jizhou1; Guan, Fang1,2; Zhai, Xiaofan1; Zhao, Shengjun1,3; Li, Ke1,2; Hou, Baorong1
|
| 刊名 | INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
 |
| 出版日期 | 2017-03-01 |
| 卷号 | 12期号:3页码:2315-2328 |
| 关键词 | Carbon steel SRB Corrosion Rust layer |
| 英文摘要 | In this work, a pure Bacillus sp. and a consortium of microbes were isolated from inner rust layer of carbon steel from marine environment. Corrosion behavior of Q235 carbon steel was investigated in the presence and in the absence of Bacillus sp. and with consortium of microbes separately. Weight loss, electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM) and energy dispersive spectrum (EDS) tests were conducted to observe the influence on corrosion behavior of carbon steel in the presence and in the absence of bacteria. The results showed that corrosion potential (E-corr) decreased and the corrosion current density increased in the presence of bacteria, in contrast with the sterile medium with the same exposure time interval. The weight loss was observed and micrometer-scale pitting further confirmed by SEM on the carbon steel surface in the presence of bacteria especially with the Bacillus sp. Most importantly in the present work Bacillus sp. behaved like sulfate reducing bacteria (SRB). Further, it was confirmed that in natural environment Bacillus sp. could also act like sulfate-reducing bacteria and deteriorating carbon steel, especially in the form of localized pitting/corrosion. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000397256700053 |
| 版本 | 出版稿 |
| 源URL | [http://ir.qdio.ac.cn/handle/337002/136729]  |
| 专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
| 作者单位 | 1.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China 2.Univ Chinese Acad Sci, 19 Jia Yuquan Rd, Beijing 100049, Peoples R China 3.Harbin Inst Technol Weihai, Marine Sch Sci & Technol, 2-W Wenhua Rd, Weihai City 264209, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, Meixia,Liu, Haixia,Karn, Santosh Kr,et al. Corrosion Behavior of Q235 Carbon Steel in Presence of H2S Producing Bacillus sp and a Consortium of Microbes Isolated from Inner Rust Layer[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,2017,12(3):2315-2328. |
| APA | Zhang, Meixia.,Liu, Haixia.,Karn, Santosh Kr.,Duan, Jizhou.,Guan, Fang.,...&Hou, Baorong.(2017).Corrosion Behavior of Q235 Carbon Steel in Presence of H2S Producing Bacillus sp and a Consortium of Microbes Isolated from Inner Rust Layer.INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,12(3),2315-2328. |
| MLA | Zhang, Meixia,et al."Corrosion Behavior of Q235 Carbon Steel in Presence of H2S Producing Bacillus sp and a Consortium of Microbes Isolated from Inner Rust Layer".INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 12.3(2017):2315-2328. |
入库方式： OAI收割
来源：海洋研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。