Effect of AB(5) alloy on Ti0.10Zr0.15V0.35Cr0.10Ni0.30 hydrogen storage alloy
文献类型：期刊论文
| 作者 | Wang YZ ; Zhao MS ; Wang LM |
| 刊名 | journal of applied electrochemistry
 |
| 出版日期 | 2009 |
| 卷号 | 39期号:9页码:1565-1572 |
| 关键词 | METAL HYDRIDE ELECTRODES SOLID-SOLUTION ALLOYS ELECTROCHEMICAL PROPERTIES DETERIORATION BEHAVIOR PHASE STRUCTURES MICROSTRUCTURE NI TI SUBSTITUTION LANI5 |
| ISSN号 | 0021-891x |
| 通讯作者 | zhao ms |
| 中文摘要 | the structure and electrochemical characteristics of melted composite ti0.10zr0.15v0.35cr0.10ni0.30 + x% lani4al0.4mn0.3co0.3 (x = 0, 1, 5) hydrogen storage alloys have been investigated systematically. xrd shows that though the main phase of the matrix alloy remains unchanged after lani4al0.4mn0.3co0.3 alloy is added, a new specimen is formed. the amount of the new specimen increases with increasing x. sem-eds analysis indicates that the v-based solid solution phase is mainly composed of v, cr and ni; c14 laves phase is mainly composed of ni, zr and v; the new specimen containing la is mainly composed of zr, v and ni. the electrochemical measurements suggest that the activation performance, the low temperature discharge ability, the high rate discharge ability and the cyclic stability of composite alloy electrodes increase greatly with the growth of x. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000269012900019 |
| 公开日期 | 2010-05-04 |
| 源URL | [http://202.98.16.49/handle/322003/11579]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Wang YZ,Zhao MS,Wang LM. Effect of AB(5) alloy on Ti0.10Zr0.15V0.35Cr0.10Ni0.30 hydrogen storage alloy[J]. journal of applied electrochemistry,2009,39(9):1565-1572. |
| APA | Wang YZ,Zhao MS,&Wang LM.(2009).Effect of AB(5) alloy on Ti0.10Zr0.15V0.35Cr0.10Ni0.30 hydrogen storage alloy.journal of applied electrochemistry,39(9),1565-1572. |
| MLA | Wang YZ,et al."Effect of AB(5) alloy on Ti0.10Zr0.15V0.35Cr0.10Ni0.30 hydrogen storage alloy".journal of applied electrochemistry 39.9(2009):1565-1572. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。