Architectures of Strontium Hydroxyapatite Microspheres: Solvothermal Synthesis and Luminescence Properties
文献类型：期刊论文
| 作者 | Zhang CM ; Cheng ZY ; Yang PP ; Xu ZH ; Peng C ; Li GG ; Lin J |
| 刊名 | langmuir
 |
| 出版日期 | 2009 |
| 卷号 | 25期号:23页码:13591-13598 |
| 关键词 | CARBOXYLIC-ACID SOLVOLYSIS WHITE-LIGHT EMISSION SOL-GEL PROCESS HYDROTHERMAL SYNTHESIS PHOTOLUMINESCENCE PROPERTIES HIERARCHICAL MICROSPHERES OPTICAL-PROPERTIES GROWTH NANOSTRUCTURES NANOPARTICLES |
| ISSN号 | 0743-7463 |
| 通讯作者 | lin j |
| 中文摘要 | strontium hydroxyapatite (sr-5(po4)(3)oh, srhap) microspheres with 3d architectures have been successfully prepared through a efficient and facile solvothermal process. the experimental results indicate that the srhap microspheres are composed of a large amount of nanosheets, which are assembled in a radial form from the center to the surface of the microspheres. the as-obtained srhap samples show an intense and bright blue emission from 350 to 570 nm centered at 427 nm (cie coordinates: x = 0.153, y = 0.081; lifetime: 9.2 ns; quantum efficiency: 31%) under long-wavelength uv light excitation (344 nm). this blue emission might result from the co2 center dot- radical impurities in the crystal lattice. furthermore, the surfactants ctab and trisodium citrate have an obvious impact on the morphologies and the luminescence properties of the products, respectively. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000271947700050 |
| 公开日期 | 2010-05-27 |
| 源URL | [http://202.98.16.49/handle/322003/11987]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Zhang CM,Cheng ZY,Yang PP,et al. Architectures of Strontium Hydroxyapatite Microspheres: Solvothermal Synthesis and Luminescence Properties[J]. langmuir,2009,25(23):13591-13598. |
| APA | Zhang CM.,Cheng ZY.,Yang PP.,Xu ZH.,Peng C.,...&Lin J.(2009).Architectures of Strontium Hydroxyapatite Microspheres: Solvothermal Synthesis and Luminescence Properties.langmuir,25(23),13591-13598. |
| MLA | Zhang CM,et al."Architectures of Strontium Hydroxyapatite Microspheres: Solvothermal Synthesis and Luminescence Properties".langmuir 25.23(2009):13591-13598. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。