Tribological characteristics and wear mechanisms of NiMoAl composite coatings in reversible temperature cycles from RT to 900 ℃
文献类型：期刊论文
| 作者 | Zhong HQ(钟火清)1,2; Feng XC(丰晓春)1,2; Jia JH(贾均红)1 ; Yi GW(易戈文)1; Yi GW(易戈文)
|
| 刊名 | Tribology International
 |
| 出版日期 | 2017 |
| 卷号 | 114页码:48-56 |
| 关键词 | Wide-temperature range Plasma spray Reversible temperature cycles Composite coating |
| ISSN号 | 0301-679X |
| 通讯作者 | 易戈文 |
| 英文摘要 | In an effort to investigate the influence of temperature cycles and of tribo-layers formed at high temperatures on the tribological properties and mechanisms of wide-temperature range lubricating materials at low temperatures, the tribological characteristics of atmospheric plasma sprayed NiMoAk-6Al2O310Ag composite coatings in reversible temperature cycles were investigated. The results indicated that the tribo-layers formed at low temperature have no evident effect on the friction coefficients during subsequent testing at elevated temperatures, while the lubricating film formed at 900 ℃ decreased the friction coefficient in a subsequent RT test evidently. The lowest friction coefficient at 900 ℃ was attributed to the formation of lubricating film on the worn surface, which was mainly consisting of NiO and Ag2MoO4 nanoparticles. |
| 学科主题 | 材料科学与物理化学 |
| 收录类别 | SCI |
| 资助信息 | the National Natural Science Foundation of China (Grant Nos. 51471181;51575505;51675508) |
| 语种 | 英语 |
| WOS记录号 | WOS:000404815600006 |
| 源URL | [http://210.77.64.217/handle/362003/22093]  |
| 专题 | 兰州化学物理研究所_固体润滑国家重点实验室 |
| 通讯作者 | Yi GW(易戈文) |
| 作者单位 | 1.Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhong HQ,Feng XC,Jia JH,et al. Tribological characteristics and wear mechanisms of NiMoAl composite coatings in reversible temperature cycles from RT to 900 ℃[J]. Tribology International,2017,114:48-56. |
| APA | Zhong HQ,Feng XC,Jia JH,Yi GW,&易戈文.(2017).Tribological characteristics and wear mechanisms of NiMoAl composite coatings in reversible temperature cycles from RT to 900 ℃.Tribology International,114,48-56. |
| MLA | Zhong HQ,et al."Tribological characteristics and wear mechanisms of NiMoAl composite coatings in reversible temperature cycles from RT to 900 ℃".Tribology International 114(2017):48-56. |
入库方式： OAI收割
来源：兰州化学物理研究所
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。