Stress corrosion cracking of fusion boundary for 316L/52M dissimilar metal weld joints in borated and lithiated high temperature water
文献类型：期刊论文
| 作者 | Zhu, Ruolin ; Wang, Jianqiu ; Zhang, Zhiming ; Han, En-Hou |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2017-05-15 |
| 卷号 | 120页码:219-230 |
| 关键词 | Stainless steel Nickel SEM Welding Stress corrosion |
| ISSN号 | 0010-938X |
| 通讯作者 | Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China. |
| 中文摘要 | The stress corrosion cracking (SCC) crack growth rates (CGRs) at the fusion boundary (FB) for 316L/52M weld joints were measured using direct current potential drop systems in borated and lithiated high temperature water. The cracks propagated along the FB and were blocked after propagating into the composition transient zone. The cracking mode is both intergranular and transgranular. The CGRs at the FB are similar to those in the heat-affected zone (HAZ) in oxygenated water, but slightly higher than those in the HAZ in hydrogenated water. The temperature dependences of CGR in both hydrogenated and oxygenated water are discussed. (C) 2017 Elsevier Ltd. All rights reserved. |
| 学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 收录类别 | SCI |
| 资助信息 | CAS [QYZDY-SSW-JSC012]; National Natural Science Foundation of China [51301183] |
| 语种 | 英语 |
| 公开日期 | 2017-08-17 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/78137]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Zhu, Ruolin,Wang, Jianqiu,Zhang, Zhiming,et al. Stress corrosion cracking of fusion boundary for 316L/52M dissimilar metal weld joints in borated and lithiated high temperature water[J]. CORROSION SCIENCE,2017,120:219-230. |
| APA | Zhu, Ruolin,Wang, Jianqiu,Zhang, Zhiming,&Han, En-Hou.(2017).Stress corrosion cracking of fusion boundary for 316L/52M dissimilar metal weld joints in borated and lithiated high temperature water.CORROSION SCIENCE,120,219-230. |
| MLA | Zhu, Ruolin,et al."Stress corrosion cracking of fusion boundary for 316L/52M dissimilar metal weld joints in borated and lithiated high temperature water".CORROSION SCIENCE 120(2017):219-230. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。