Origin of unusual fracture in stirred zone for friction stir welded 2198-T8 Al-Li alloy joints
文献类型：期刊论文
| 作者 | Tao, Y. ; Ni, D. R. ; Xiao, B. L. ; Ma, Z. Y. ; Wu, W. ; Zhang, R. X. ; Zeng, Y. S. |
| 刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
 |
| 出版日期 | 2017-05-02 |
| 卷号 | 693页码:1-13 |
| ISSN号 | 0921-5093 |
| 关键词 | Friction stir welding Aluminum-Lithium alloys Microstructure Fracture behavior |
| 通讯作者 | Ni, DR (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China. ; Zeng, YS (reprint author), AVIC Beijing Aeronaut Mfg Technol Res Inst, Beijing 100024, Peoples R China. |
| 中文摘要 | Friction stir welded (FSW) joints of conventional precipitation-hardened aluminum alloys usually fracture in the lowest hardness zone (LHZ) during tension testing. However, all of the FSW joints of a 2198-T8 Al-Li alloy fractured in the stirred zone (SZ) instead of the LHZ with the welding parameters of 800 rpm-200 mm/min and 1600 rpm-200 mm/min under the condition that no welding defects existed in the SZ. The experiment results revealed that lazy S was not the dominant factor resulting in the unusual fracture. The SZ consisted of three subzones, i.e., the shoulder-affected zone, the pin-affected zone, and the transition zone between them. While the former two zones were characterized by fine and equiaxed recrystallized grains, incompletely dynamically recrystallized microstructure containing coarse elongated non-recrystallized grains was observed in the transition zone. The transition zone exhibited the lowest average Taylor factor in the SZ, resulting in a region that was crystallographically weak. Furthermore, obvious lithium segregation at grain boundaries was observed in the transition zone via time-of-flight secondary ion mass spectroscopy analysis, but not in the shoulder affected zone or the pin-affected zone. The combined actions of both the two factors resulted in the appearance of preferential intergranular fracture in the transition zone and eventually caused the failure in the SZ. The lithium segregation at grain boundaries in the transition zone was closely associated with both the segregation in the base material and the partially dynamically recrystallized microstructure resulting from the inhomogeneous plastic deformation in the SZ. |
| 学科主题 | Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 资助信息 | National Natural Science Foundation of China [51331008] |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2017-08-17 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/78147]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Tao, Y.,Ni, D. R.,Xiao, B. L.,et al. Origin of unusual fracture in stirred zone for friction stir welded 2198-T8 Al-Li alloy joints[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2017,693:1-13. |
| APA | Tao, Y..,Ni, D. R..,Xiao, B. L..,Ma, Z. Y..,Wu, W..,...&Zeng, Y. S..(2017).Origin of unusual fracture in stirred zone for friction stir welded 2198-T8 Al-Li alloy joints.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,693,1-13. |
| MLA | Tao, Y.,et al."Origin of unusual fracture in stirred zone for friction stir welded 2198-T8 Al-Li alloy joints".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 693(2017):1-13. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。