Corrosion resistance of chromised and aluminised coatings in wet CO2 gas at 650 degrees C
文献类型:期刊论文
作者 | Thuan Dinh Nguyen ; Peng, Xiao ; Zhang, Jianqiang ; Young, David J. |
刊名 | SURFACE & COATINGS TECHNOLOGY
![]() |
出版日期 | 2017-04-25 |
卷号 | 316页码:226-238 |
关键词 | Pack cementation Diffusion coatings CO2 corrosion |
ISSN号 | 0257-8972 |
通讯作者 | Young, DJ (reprint author), Univ New South Wales, Sch Mat Sci & Engn, Sydney, NSW 2052, Australia. |
中文摘要 | Four chromised and aluminised coatings, with and without an intermediate nickel layer, were produced by pack cementation. The nickel layer was deposited onto a T91 steel substrate prior to the pack cementation process to limit interdiffusion of elements between the coatings and the substrate. The coated and uncoated steels were exposed to Ar-20CO(2)-20H(2)O gas at 650 degrees C. The uncoated steel formed a thick, iron-rich oxide scale, whereas all coated samples formed thin, protective chromia or alumina scales. The uncoated steel was carburised under its scale. Carbide precipitates were formed in the chromized coatings before and after reactions, but not in the aluminised coatings. (C) 2017 Elsevier B.V. All rights reserved. |
学科主题 | Materials Science, Coatings & Films ; Physics, Applied |
收录类别 | SCI |
资助信息 | Early Career Research Grant (University of New South Wales) [PS40715] |
语种 | 英语 |
公开日期 | 2017-08-17 |
源URL | [http://ir.imr.ac.cn/handle/321006/78177] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Thuan Dinh Nguyen,Peng, Xiao,Zhang, Jianqiang,et al. Corrosion resistance of chromised and aluminised coatings in wet CO2 gas at 650 degrees C[J]. SURFACE & COATINGS TECHNOLOGY,2017,316:226-238. |
APA | Thuan Dinh Nguyen,Peng, Xiao,Zhang, Jianqiang,&Young, David J..(2017).Corrosion resistance of chromised and aluminised coatings in wet CO2 gas at 650 degrees C.SURFACE & COATINGS TECHNOLOGY,316,226-238. |
MLA | Thuan Dinh Nguyen,et al."Corrosion resistance of chromised and aluminised coatings in wet CO2 gas at 650 degrees C".SURFACE & COATINGS TECHNOLOGY 316(2017):226-238. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。