Influences of Cooling Rate After Solution Treatment on Microstructural Evolution and Mechanical Properties of Superalloy Rene 80
文献类型：期刊论文
| 作者 | Gao, Shuang ; Hou, Jie-Shan ; Dong, Kai-Xin ; Zhou, Lan-Zhang |
| 刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS
 |
| 出版日期 | 2017-03-01 |
| 卷号 | 30期号:3页码:261-271 |
| 关键词 | Ni-based superalloy Cooling rate gamma' Precipitates Ripening theory Heat treatment Microstructural evolution |
| ISSN号 | 1006-7191 |
| 通讯作者 | Zhou, LZ (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China. |
| 中文摘要 | Influences of the cooling rate after solution treatment on microstructural evolution and mechanical properties of Rene 80 nickel-based superalloy were investigated by optical microscopy, scanning electron microscopy, transmission electron microscopy and mechanical test. Results showed that the high cooling rate decreased the size of secondary gamma' particles in the supersaturated matrix, but led to a high coarsening rate of gamma' particles during subsequent aging treatment. Despite various coarsening rates, the size and morphology of gamma' particles in the final microstructures of all samples were close due to the long enough holding time to an equilibrium state. During the aging of 870 degrees C/2 h, primary MC started to decompose with the carbide reaction: MC + gamma -> M6C or M23C6 + gamma'. And a number of observations showed that the coarsening of gamma' particles on grain boundaries resulted in the depletion of gamma' during aging treatment. The test results indicated that high cooling rate resulted in the presence of quench crack, and the air cooling method following solution treatment was an optimum heat treatment method for Rene 80. |
| 学科主题 | Metallurgy & Metallurgical Engineering |
| 收录类别 | SCI |
| 资助信息 | National Natural Science Foundation of China [51571191] |
| 语种 | 英语 |
| 公开日期 | 2017-08-17 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/78255]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Gao, Shuang,Hou, Jie-Shan,Dong, Kai-Xin,et al. Influences of Cooling Rate After Solution Treatment on Microstructural Evolution and Mechanical Properties of Superalloy Rene 80[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2017,30(3):261-271. |
| APA | Gao, Shuang,Hou, Jie-Shan,Dong, Kai-Xin,&Zhou, Lan-Zhang.(2017).Influences of Cooling Rate After Solution Treatment on Microstructural Evolution and Mechanical Properties of Superalloy Rene 80.ACTA METALLURGICA SINICA-ENGLISH LETTERS,30(3),261-271. |
| MLA | Gao, Shuang,et al."Influences of Cooling Rate After Solution Treatment on Microstructural Evolution and Mechanical Properties of Superalloy Rene 80".ACTA METALLURGICA SINICA-ENGLISH LETTERS 30.3(2017):261-271. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。