The relationship of dislocation and vacancy cluster with yield strength in magnetic annealed UFG 1050 aluminum alloy
文献类型：期刊论文
| 作者 | Cao, Yiheng ; He, Lizi ; Cao, Xingzhong ; Zhang, Peng ; Wang, Baoyi ; Zhou, Yizhou ; Wang, Ping ; Cui, Jianzhong |
| 刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
 |
| 出版日期 | 2017-01-02 |
| 卷号 | 679页码:417-427 |
| 关键词 | Magnetic field Ultrafine grained 1050 alloy Annealing Yield strength Dislocation Vacancy cluster |
| ISSN号 | 0921-5093 |
| 通讯作者 | He, LZ (reprint author), Northeastern Univ, Minist Educ, Key Lab Electromagnet Proc Mat, Shenyang 110819, Peoples R China. |
| 中文摘要 | The evolutions of tensile properties and microstructures of ultrafine grained (UFG) 1050 aluminum alloy after annealing at 90-210 degrees C for 4 h without and with 12 T high magnetic field were investigated by tensile test, electron back scattering diffraction pattern (EBSD), transmission electron microscopy (TEM) and positron annihilation lifetime spectroscopy (PALS). When annealing temperature increases from 90 degrees C to 150 degrees C, the yield strength (YS) of UFG 1050 aluminum alloy increases, it is because that the increase in the density of vacancy clusters due to the activated monovacancies and the high angle boundaries (HABs) having more stable structures, both of them can act as effective barriers to dislocation motion during tensile deformation. When annealing at 210 degrees C, the YS of UFG 1050 aluminum alloy deceases, it is because that the decrease in the vacancy clusters density due to the thermally activated the vacancy clusters annihilating at sinks and the dislocation density decreases. The YS of magnetic annealed samples are lower at 90 degrees C and 150 degrees C due to the lower density of dislocations and vacancy clusters. The difference of YS between samples annealed without and with magnetic field disappears at 210 degrees C due to the sharply reduced strain hardening stage. |
| 学科主题 | Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 收录类别 | SCI |
| 资助信息 | National Natural Science Foundation of China [51574076]; Fundamental Research Funds for the Central University [N150902001] |
| 语种 | 英语 |
| 公开日期 | 2017-08-17 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/78356]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Cao, Yiheng,He, Lizi,Cao, Xingzhong,et al. The relationship of dislocation and vacancy cluster with yield strength in magnetic annealed UFG 1050 aluminum alloy[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2017,679:417-427. |
| APA | Cao, Yiheng.,He, Lizi.,Cao, Xingzhong.,Zhang, Peng.,Wang, Baoyi.,...&Cui, Jianzhong.(2017).The relationship of dislocation and vacancy cluster with yield strength in magnetic annealed UFG 1050 aluminum alloy.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,679,417-427. |
| MLA | Cao, Yiheng,et al."The relationship of dislocation and vacancy cluster with yield strength in magnetic annealed UFG 1050 aluminum alloy".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 679(2017):417-427. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。