Microstructures and properties of Mg-7Gd alloy containing Y
文献类型：期刊论文
| 作者 | Peng QM ; Wu YM ; Fang DQ ; Meng J ; Wang LM |
| 刊名 | journal of alloys and compounds
 |
| 出版日期 | 2007 |
| 卷号 | 430期号:1-2页码:252-256 |
| 关键词 | RARE EARTH ALLOYS MG-GD ALLOYS ZR ALLOYS MAGNESIUM YTTRIUM PRECIPITATION TEMPERATURE DYSPROSIUM GADOLINIUM |
| ISSN号 | 0925-8388 |
| 通讯作者 | wang lm |
| 中文摘要 | mg-7 mass%gd-x mass%y (x = 0, 1, 3 and 5) alloys were prepared by casting method, and the microstructures, age hardening behavior and mechanical properties have been investigated. the results show that the addition of y to the binary mg-7gd alloy could reduce the grain size of the as-cast alloys, and enhance the age hardening response and improve mechanical properties during the investigated temperature range. the mg-7gd-5y alloy exhibits maximum ultimate tensile strength and yield strength at peak hardness, and the values are 258 and 167 mpa at room temperature, and 212 and 140 mpa at 250 degrees c, respectively, which is about 1.8 times as high as the mg-7gd binary alloy. when x is more than 3, the amount of mg-5 (gd,y) phase is observed at the peak hardness of aged alloys. the significant improvement of the tensile strength at peak hardness is mainly attributed to the fine dispersion of the beta-mg-5(gd,y) precipitate. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000244826200045 |
| 公开日期 | 2010-07-13 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/13705]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Peng QM,Wu YM,Fang DQ,et al. Microstructures and properties of Mg-7Gd alloy containing Y[J]. journal of alloys and compounds,2007,430(1-2):252-256. |
| APA | Peng QM,Wu YM,Fang DQ,Meng J,&Wang LM.(2007).Microstructures and properties of Mg-7Gd alloy containing Y.journal of alloys and compounds,430(1-2),252-256. |
| MLA | Peng QM,et al."Microstructures and properties of Mg-7Gd alloy containing Y".journal of alloys and compounds 430.1-2(2007):252-256. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。