Microstructures and mechanical properties of Mg-8Gd-0.6Zr-xNd (x=0, 1, 2 and 3 mass%) alloys
文献类型:期刊论文
作者 | Peng QM ; Wu YM ; Fang DQ ; Meng J ; Wang LM |
刊名 | journal of materials science
![]() |
出版日期 | 2007 |
卷号 | 42期号:11页码:3908-3913 |
关键词 | RARE EARTH ALLOYS Y-ZR ALLOYS MG-Y MAGNESIUM PRECIPITATION PERFORMANCE DYSPROSIUM GADOLINIUM YTTRIUM |
ISSN号 | 0022-2461 |
通讯作者 | wang lm |
中文摘要 | mg-8gd-0.6zr-xnd (x = 0, 1, 2 and 3 mass%) alloys were prepared by metal mould casting method, and the microstructures, age hardening responses and mechanical properties have been investigated. the microhardness of the as-cast alloys is increased with increasing nd content. the age hardening behavior and mechanical properties are enhanced significantly by adding nd element. the peak ageing hardness of the mg-8gd-0.6zr-3nd alloy is 103, it is about 1.3 times more than that of the mg-8gd-0.6zr alloy. the aged mg-8gd-0.6zr-3nd alloy exhibits maximum ultimate tensile strength and yield strength, and the values are 271 and 205 mpa at room temperature, 205 mpa and 150 mpa at 250 degrees c, respectively. which are about 2 times higher than those of mg-8gd-0.6zr alloy. the improved hardness and strength are mainly attributed to the fine dispersiveness of mg5re and mg12re precipitates in the alloy. |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000247375100030 |
公开日期 | 2010-07-13 |
源URL | [http://ir.ciac.jl.cn/handle/322003/13713] ![]() |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Peng QM,Wu YM,Fang DQ,et al. Microstructures and mechanical properties of Mg-8Gd-0.6Zr-xNd (x=0, 1, 2 and 3 mass%) alloys[J]. journal of materials science,2007,42(11):3908-3913. |
APA | Peng QM,Wu YM,Fang DQ,Meng J,&Wang LM.(2007).Microstructures and mechanical properties of Mg-8Gd-0.6Zr-xNd (x=0, 1, 2 and 3 mass%) alloys.journal of materials science,42(11),3908-3913. |
MLA | Peng QM,et al."Microstructures and mechanical properties of Mg-8Gd-0.6Zr-xNd (x=0, 1, 2 and 3 mass%) alloys".journal of materials science 42.11(2007):3908-3913. |
入库方式: OAI收割
来源:长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。