Long-term anticorrosion behaviour of polyaniline on mild steel
文献类型：期刊论文
| 作者 | Chen Y ; Wang XH ; Li J ; Lu JL ; Wang FS |
| 刊名 | corrosion science
 |
| 出版日期 | 2007 |
| 卷号 | 49期号:7页码:3052-3063 |
| 关键词 | ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY ELECTROACTIVE CONDUCTING POLYMERS CORROSION PROTECTION ORGANIC COATINGS PART 1 METALS EIS PREVENTION MECHANISM PROGRESS |
| ISSN号 | 0010-938x |
| 通讯作者 | wang xh |
| 中文摘要 | anticorrosion performances of polyaniline emeraldine base/epoxy resin (eb/er) coating on mild steel in 3.5% nacl solutions of various ph values were investigated by electrochemical impedance spectroscopy (eis) for 150 days. in neutral solution (ph 6.1), eb/er coating offered very efficient corrosion protection with respect to pure er coating, especially when eb content was 5-10%. the impedance at 0.1 hz of the coating increased in the first 1-40 immersion days and then remained constant above 10(9) omega cm(2) until 150 days, which in combination with the observation of a fe2o3/fe3o4 passive film formed on steel confirmed that the protection of eb was mainly anodic. in acidic or basic solution (ph 1 or 13), eb/er coating also performed much better than pure er coating. however, these media weakened the corrosion resistance due to breakdown of the passive film or deterioration of the er binder. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000248039500019 |
| 公开日期 | 2010-07-13 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/14141]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Chen Y,Wang XH,Li J,et al. Long-term anticorrosion behaviour of polyaniline on mild steel[J]. corrosion science,2007,49(7):3052-3063. |
| APA | Chen Y,Wang XH,Li J,Lu JL,&Wang FS.(2007).Long-term anticorrosion behaviour of polyaniline on mild steel.corrosion science,49(7),3052-3063. |
| MLA | Chen Y,et al."Long-term anticorrosion behaviour of polyaniline on mild steel".corrosion science 49.7(2007):3052-3063. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。