Up-conversion spectrum properties of the oxy-fluoride glass co-doped with Er3+ and Yb3+
文献类型：期刊论文
| 作者 | Liang HL ; Yang KS ; Zhang XY ; Machida K ; Meng H |
| 刊名 | journal of alloys and compounds
 |
| 出版日期 | 2006 |
| 卷号 | 408页码:835-837 |
| 关键词 | ENERGY-TRANSFER LUMINESCENCE CERAMICS IONS |
| ISSN号 | 0925-8388 |
| 通讯作者 | yang ks |
| 中文摘要 | up-conversion of 45pbf(2)-45geo(2)-10wo(3) oxy-fluoride glasses co-doped with yb3+ and er3+ ions were prepared by fusion method through melting at 1223 k and then annealing at 653 k for 4 h. transmittance of the undoped host glass was beyond 73% in a range of 0.6-2.5 mu m and the co-doped glasses still provided good transmittance beyond 50%. refractive indices of the host and co-doped glasses were 1.517 and 1.650, respectively. blue, green and red fluorescence spectra were observed in a range of 400-700 nm under 980 nm diode laser excitation. up-conversion spectra at about 410, 518, 530and 650 nm were assigned to the 4f electron transitions of h-2(9/2) -> i-4(15)/(2), h-2(15/2) -> i-4(15/2) s-4(3/2) -> i-4(15/2) and f-4(9/2) -> i-4(15/2) of er3+ ion, respectively. the mechanism of energy transfer between yb3+ and er3+ ions in the glass was analyzed. raman shift shows the non-radiative relaxation of the glass sample is low. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000235445300190 |
| 公开日期 | 2010-08-17 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/16557]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Liang HL,Yang KS,Zhang XY,et al. Up-conversion spectrum properties of the oxy-fluoride glass co-doped with Er3+ and Yb3+[J]. journal of alloys and compounds,2006,408:835-837. |
| APA | Liang HL,Yang KS,Zhang XY,Machida K,&Meng H.(2006).Up-conversion spectrum properties of the oxy-fluoride glass co-doped with Er3+ and Yb3+.journal of alloys and compounds,408,835-837. |
| MLA | Liang HL,et al."Up-conversion spectrum properties of the oxy-fluoride glass co-doped with Er3+ and Yb3+".journal of alloys and compounds 408(2006):835-837. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。