STUDY ON THE NON-STIOCHIOMETRIC SNO2-X NANOCRYSTALLINE MATERIAL BY XRD, XPS AND ESR
文献类型：期刊论文
| 作者 | LI Q ; ZENG GF ; ZHAN RY ; XI SQ |
| 刊名 | acta chimica sinica
 |
| 出版日期 | 1995 |
| 卷号 | 53期号:4页码:381-385 |
| 关键词 | ELECTRON |
| ISSN号 | 0567-7351 |
| 通讯作者 | zeng gb |
| 中文摘要 | nonstiochiometric sno2-x nanocrystalline material were successfully prepared through sol-gel process using anhydrous stannic chloride and iso-propyl alcohol. tem observation shows that the mean diameter of the powder sintered at 700 degrees c for 2 hours is about 20 nm. by the investigation of xrd and esr, we can conclude that the sample sintered at 300 degrees c for 2 hours was amorphous and it grew into nanocrystalline with the oxygen vacancies and defects when sintered at 700 degrees c for 2 hours. using these conclusion, the esr signals and the difference between the two sno2-x samples are explained. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 中文 |
| 公开日期 | 2010-12-30 ; 2011-06-10 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/26625]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | LI Q,ZENG GF,ZHAN RY,et al. STUDY ON THE NON-STIOCHIOMETRIC SNO2-X NANOCRYSTALLINE MATERIAL BY XRD, XPS AND ESR[J]. acta chimica sinica,1995,53(4):381-385. |
| APA | LI Q,ZENG GF,ZHAN RY,&XI SQ.(1995).STUDY ON THE NON-STIOCHIOMETRIC SNO2-X NANOCRYSTALLINE MATERIAL BY XRD, XPS AND ESR.acta chimica sinica,53(4),381-385. |
| MLA | LI Q,et al."STUDY ON THE NON-STIOCHIOMETRIC SNO2-X NANOCRYSTALLINE MATERIAL BY XRD, XPS AND ESR".acta chimica sinica 53.4(1995):381-385. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。