Preperation and Photoluminescent Properties of Ca2AlSi3O2N5:Sm3+ Phosphor
文献类型:期刊论文
作者 | Wang F(王璠); Qiao XS(乔旭升); Wu YM(吴一民); Fan XP(樊先平); Wu LA(吴立昂); Wan J(万军) |
刊名 | 稀有金属材料与工程 |
出版日期 | 2016 |
卷号 | 45期号:S1页码:550 |
通讯作者 | onedream@zju.edu.cn ; fanxp@zju.edu.cn |
中文摘要 | 采用原位共沉淀与气氛还原氮化相结合的方法,在1100℃下制备出Ca2AlSi3O_2N5:Sm~(3+)。使用X射线衍射仪(XRD)、场发射扫描电子显微镜(FE-SEM)以及稳态瞬态荧光光谱仪(PL)对合成产物的结构、微观形貌和发光特性进行了研究。在287nm紫外光激发下,测得Ca2AlSi3O_2N5:Sm~(3+)的发射光谱为1个多峰宽谱,主峰分别为602nm(4G5/2→6H7/2)和650nm(4G5/2→6H9/2)。研究了Sm~(3+)掺杂浓度对Ca2AlSi3O_2N5:Sm~(3+)红光荧 |
英文摘要 | Ca2AlSi3O2N5:Sm3+ phosphor was prepared by a combination of in-situ co-precipitation method with a gas-reduction-nitridation method at 1100 degrees C. Its structure and luminescent properties were investigated with XRD and PL. The emission spectrum of Ca2AlSi3O2N5:Sm3+ shows several pesks at 602 nm ((4)G(5/2) -> H-6(7/2)), and 650 nm ((4)G(5/2) -> H-6(9/2)) under 287 nm excitation. The effect of the doping concentration of Sm3+ activator on the luminescence properties was studied. It is found that the luminescence intensity increases with increasing of Sm3+ doping concentration within limits, and then decreases. The photoluminescence intensity reaches the highest when the Sm3+ doping concentration is 1 mol%. |
资助信息 | 浙江省重点创新团队资助(2009R50010) |
收录类别 | SCI |
WOS记录号 | WOS:000392168800122 |
源URL | [http://ir.siom.ac.cn/handle/181231/28773] |
专题 | 上海光学精密机械研究所_其他 |
作者单位 | 中国科学院上海光学精密机械研究所 |
推荐引用方式 GB/T 7714 | Wang F,Qiao XS,Wu YM,et al. Preperation and Photoluminescent Properties of Ca2AlSi3O2N5:Sm3+ Phosphor[J]. 稀有金属材料与工程,2016,45(S1):550. |
APA | 王璠,乔旭升,吴一民,樊先平,吴立昂,&万军.(2016).Preperation and Photoluminescent Properties of Ca2AlSi3O2N5:Sm3+ Phosphor.稀有金属材料与工程,45(S1),550. |
MLA | 王璠,et al."Preperation and Photoluminescent Properties of Ca2AlSi3O2N5:Sm3+ Phosphor".稀有金属材料与工程 45.S1(2016):550. |
入库方式: OAI收割
来源:上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。