High transparency Cr,Nd:LuAG ceramics prepared with MgO additive
文献类型：期刊论文
| 作者 | Zhang, Pande; Chai, Baoyan; Jiang, Benxue; Jiang, Yiguang; Chen, Shuilin; Gan, Qijun; Fan, Jintai; Mao, Xiaojian; Zhang, Long |
| 刊名 | J. Eur. Ceram. Soc.
 |
| 出版日期 | 2017 |
| 卷号 | 37期号:6页码:2459 |
| 通讯作者 | jiangsic@foxmail.com ; lzhang@siom.ac.cn |
| 英文摘要 | Cr (0.2 at.%) and Nd (0.8 at.%) co-doped Lu3Al5O12 ceramics were fabricated with MgO as the sintering additive. The addition of a small amount of MgO can affect the grain boundary mobility and influence the number and location of micropores in ceramics during the sintering process. The results show that when the MgO content is 0.02 wt.%, high-transparency Cr,Nd:LuAG ceramics can be obtained by vacuum sintering at 1670 degrees C for 5 h followed by hot isostatic pressing (HIP) post-sintering at 1750 degrees C in an argon atmosphere (P = 200 MPa) for 5 h. The optimum in-line transmittance of the HIPed Cr,Nd:LuAG ceramics (3 mm thick) is 83.5% at a wavelength of 840 nm and 84.0% at 710 nm. (C) 2017 Published by Elsevier Ltd. |
| 收录类别 | SCI |
| 资助信息 | National Natural Science Foundation of China [61378069, 61405221, 61308021]; Youth Innovation Promotion Association of the CAS |
| WOS记录号 | WOS:000397359300017 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/28095]  |
| 专题 | 上海光学精密机械研究所_中科院强激光材料重点实验室 |
| 作者单位 | 中国科学院上海光学精密机械研究所 |
| 推荐引用方式 GB/T 7714 | Zhang, Pande,Chai, Baoyan,Jiang, Benxue,et al. High transparency Cr,Nd:LuAG ceramics prepared with MgO additive[J]. J. Eur. Ceram. Soc.,2017,37(6):2459. |
| APA | Zhang, Pande.,Chai, Baoyan.,Jiang, Benxue.,Jiang, Yiguang.,Chen, Shuilin.,...&Zhang, Long.(2017).High transparency Cr,Nd:LuAG ceramics prepared with MgO additive.J. Eur. Ceram. Soc.,37(6),2459. |
| MLA | Zhang, Pande,et al."High transparency Cr,Nd:LuAG ceramics prepared with MgO additive".J. Eur. Ceram. Soc. 37.6(2017):2459. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。