Influence of synthesis conditions on the properties of Y2O3-MgO nanopowders and sintered nanocomposites
文献类型：期刊论文
| 作者 | Xie, Junxi; Mao, Xiaojian; Zhu, Qiangqiang; Jiang, Benxue; Zhang, Long |
| 刊名 | J. Eur. Ceram. Soc.
 |
| 出版日期 | 2017 |
| 卷号 | 37期号:13页码:4095 |
| 通讯作者 | maoxiaojian@outlook.com ; lzhang@siom.ac.cn |
| 英文摘要 | In this study, a citrate-nitrate combustion method was applied to synthesize composite Y2O3-MgO nanopowders. In order to optimize the synthesis condition to support sufficient combustion, the molar ratio of citric acid to nitrate (c/n molar ratio) used in the reaction mixtures was varied between 0.17 and 0.34. Nanopowders with an average particle size of 17 nm were achieved. The properties of these nanopowders indicated that the higher molar ratios decreased the unreacted organic components and increased the amount of carbide on the surface of the oxides, which helped to inhibit the formation of carbonate groups. The amount of carbonate groups was reduced with the increasing c/n molar ratio. Y2O3-MgO nanocomposites fabricated through hot-isostatic-pressing sintering showed a uniform distribution of Y2O3 and MgO grains, which had an average size of similar to 180 nm. In addition, the absorption peaks at 1410 and 1511 cm(-1) disappeared until the c/n molar ratio reached 0.28. A high average infrared transmittance of 83% in the range of 4000-1667 cm(-1) (2.5-6 mu m) was obtained in the nanocomposites. (C) 2017 Elsevier Ltd. All rights reserved. |
| 收录类别 | SCI |
| 资助信息 | National Youth Natural Science Foundation of China [51302284, 61405221]; China Scholarship Council |
| WOS记录号 | WOS:000404704800029 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/28114]  |
| 专题 | 上海光学精密机械研究所_中科院强激光材料重点实验室 |
| 作者单位 | 中国科学院上海光学精密机械研究所 |
| 推荐引用方式 GB/T 7714 | Xie, Junxi,Mao, Xiaojian,Zhu, Qiangqiang,et al. Influence of synthesis conditions on the properties of Y2O3-MgO nanopowders and sintered nanocomposites[J]. J. Eur. Ceram. Soc.,2017,37(13):4095. |
| APA | Xie, Junxi,Mao, Xiaojian,Zhu, Qiangqiang,Jiang, Benxue,&Zhang, Long.(2017).Influence of synthesis conditions on the properties of Y2O3-MgO nanopowders and sintered nanocomposites.J. Eur. Ceram. Soc.,37(13),4095. |
| MLA | Xie, Junxi,et al."Influence of synthesis conditions on the properties of Y2O3-MgO nanopowders and sintered nanocomposites".J. Eur. Ceram. Soc. 37.13(2017):4095. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。