Wide Bandgap Engineering of beta-(Al, Ga)(2)O-3 Mixed Crystals
文献类型：期刊论文
| 作者 | Yi XZ(易学专); Xiao HL(肖海林); Shao GQ(邵刚勤); Sai QL(赛青林); Xia ZT(夏长泰); Zhou SM(周圣明) |
| 刊名 | 无机材料学报
 |
| 出版日期 | 2016 |
| 卷号 | 31期号:11页码:1258 |
| 通讯作者 | hlxiao2014@163.com ; saiql@siom.ac.cn ; xia_ct@siom.ac.cn |
| 中文摘要 | 通过光学浮区法生长了不同浓度的beta-(Al, Ga)_2O_3混晶。当Al~(3+)掺杂浓度达到0.26的时候, 晶体生长出现开裂现象。进行X射线衍射分析, 结果表明所得beta-(Al, Ga)_2O_3混晶保持了beta-Ga_2O_3的晶体结构, 晶体没有出现其他杂质相, 并且随着Al~(3+)浓度的增加, 晶格常数a、b、c减小, beta角增大; 核磁共振光谱显示Al的确进入了Ga的格位并且取代了Ga的四配位和六配位格位, 两者的比例约为1: 3。通过测试beta-(Al, Ga)_2O_3 |
| 英文摘要 | Bandgap tunable beta-Ga2O3 mixed crystals with different Al3+ concentration were grown by the optical floating zone (OFZ) method. When the nominal Al3+ doping concentration was close to 0.26, cracking appeared. The powder X-ray diffraction (XRD) revealed that beta-(Al, Ga)(2)O-3 mixed crystals kept the crystal structure of beta-Ga2O3 without foreign phases and the lattice parameters decreased with the increasing Al3+ concentration. Al-27 magic angle spinning (MAS) nuclear magnetic resonance (NMR) spectroscopy showed that Al3+ occupied Ga3+ positions and the ratio of Al3+(IV)/ Al3+(VI) was about 1:3. The transmittance spectra were measured to investigate the bandgap of beta-(Al, Ga)(2)O-3 mixed crystals. Results showed that the bandgap increased continuously with the Al3+ concentration increasing from 4.72 eV to 5.32 eV, which may extend the application of beta-Ga2O3 crystal in optoelectronic devices operating at shorter wavelength. |
| 收录类别 | SCI |
| 资助信息 | Science and Technology Commission of Shanghai Municipality [13111103700] |
| WOS记录号 | WOS:000389291000017 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/28222]  |
| 专题 | 上海光学精密机械研究所_中科院强激光材料重点实验室 |
| 作者单位 | 中国科学院上海光学精密机械研究所 |
| 推荐引用方式 GB/T 7714 | Yi XZ,Xiao HL,Shao GQ,et al. Wide Bandgap Engineering of beta-(Al, Ga)(2)O-3 Mixed Crystals[J]. 无机材料学报,2016,31(11):1258. |
| APA | 易学专,肖海林,邵刚勤,赛青林,夏长泰,&周圣明.(2016).Wide Bandgap Engineering of beta-(Al, Ga)(2)O-3 Mixed Crystals.无机材料学报,31(11),1258. |
| MLA | 易学专,et al."Wide Bandgap Engineering of beta-(Al, Ga)(2)O-3 Mixed Crystals".无机材料学报 31.11(2016):1258. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。