Damage characterization model of ceramic coating systems based on energy analysis and bending tests
文献类型：期刊论文
| 作者 | Liu HY; Wei YG(魏悦广) ; Liang LH(梁立红); Liu XH; Wang YB; Ma HS
|
| 刊名 | CERAMICS INTERNATIONAL
 |
| 出版日期 | 2018-04-01 |
| 卷号 | 44期号:5页码:4807-4813 |
| 关键词 | Ceramic coatings Damage characterization Fracture Thickness effect |
| ISSN号 | 0272-8842 |
| DOI | 10.1016/j.ceramint.2017.12.068 |
| 英文摘要 | A quantitative damage model of ceramic coating systems was developed based on their load-displacement curves obtained from three-point bending tests. According to the energy mechanism of damage, the normalized damage rate of such systems can be simply expressed using the load and the tangent slope of their load-displacement curves. The experimental results demonstrated the thickness dependence of fracture and damage. In thin coating systems, tensile failure was found to be predominant and multiple transverse cracks appeared in the coatings. In contrast, thick coating systems showed a predominance of interface shear failure and the occurrence of interface delamination. These observations are consistent with previous experimental results. The damage of the systems displayed catastrophic characteristics when the load tended to reach the failure point, i.e., the damage increased rapidly, and the damage rate displayed a power-law singularity at the failure point. These results are consistent with the damage characteristics predicted using the mathematic model. The damage evolution in the case of interface delamination in the thick coating systems was faster than that for transverse cracking in the thin coatings because of the difference in the degree of damage localization. The present model provides an effective method to elucidate the damage behavior of brittle ceramic coating systems, and hence, it is expected to greatly aid the coating design. |
| 分类号 | 一类 |
| URL标识 | 查看原文 |
| WOS关键词 | THERMAL BARRIER COATINGS ; FRACTURE CHARACTERISTICS ; SHOCK RESISTANCE ; CYCLE DURATION ; EVOLUTION ; FAILURE ; TENSILE ; TEMPERATURE ; MECHANISMS ; BEHAVIOR |
| WOS研究方向 | Materials Science, Ceramics |
| 语种 | 英语 |
| WOS记录号 | WOS:000425204400036 |
| 资助机构 | NSFC grants of China [11672296, 11372318, 11432014, 11672301] ; Chinese Academy of Sciences [XDB22040501] |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/77813]  |
| 专题 | 力学研究所_非线性力学国家重点实验室 |
| 作者单位 | 1.[Liu, H. Y. 2.Wei, Y. G. 3.Liang, L. H. 4.Liu, X. H. 5.Wang, Y. B. 6.Ma, H. S.] Chinese Acad Sci, Inst Mech, LNM, Beijing 100190, Peoples R China 7.[Liu, H. Y. 8.Wei, Y. G.] Peking Univ, Coll Engn, Beijing 100871, Peoples R China 9.[Liang, L. H.] Univ Chinese Acad Sci, Beijing 101408, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu HY,Wei YG,Liang LH,et al. Damage characterization model of ceramic coating systems based on energy analysis and bending tests[J]. CERAMICS INTERNATIONAL,2018,44(5):4807-4813. |
| APA | Liu HY,魏悦广,梁立红,Liu XH,Wang YB,&Ma HS.(2018).Damage characterization model of ceramic coating systems based on energy analysis and bending tests.CERAMICS INTERNATIONAL,44(5),4807-4813. |
| MLA | Liu HY,et al."Damage characterization model of ceramic coating systems based on energy analysis and bending tests".CERAMICS INTERNATIONAL 44.5(2018):4807-4813. |