Size-dependent damage and fracture of two-layer systems
文献类型：期刊论文
| 作者 | Liang LH(梁立红) ; Liu HY; Long H; Wei YG(魏悦广)
|
| 刊名 | ENGINEERING FRACTURE MECHANICS
 |
| 出版日期 | 2018-08-01 |
| 卷号 | 199页码:635-646 |
| 关键词 | Damage Fracture Ceramic layers Interface strength Interface toughness |
| ISSN号 | 0013-7944 |
| DOI | 10.1016/j.engfracmech.2018.06.040 |
| 英文摘要 | Two-dimensional three-point bending and four-point bending of two-layer finite element models for a ceramic layer on a metallic substrate are developed to study the damage and fracture characteristics of two-layer systems by introducing an interface cohesive zone model. The damage evolution and fracture modes of ceramic layers of different thicknesses, with loading on the metallic substrates, are compared under different loading conditions based on simulation results. Multiple surface cracks, vertical to the interface between the ceramic and metallic layers, appear in all ceramic layers under four-point bending loading and only in the thinner ceramic layers under three-point bending. For the thicker ceramic layer systems under three-point bending loading, the interface fracture between the ceramic and metallic layers is the main failure mode, agreeing with previous experimental observations. Damage and damage rate, defined by the simulated crack evolution, are found to obey a power law relation with loading and to be consistent with the theoretical predictions based on a mathematical damage model. The damage coefficient, a parameter reflecting the damage rate, is found to be size-dependent based on the simulation and experimental results, and its energy mechanism is discussed. The damage is slower for the thinner ceramic layers with a smaller damage coefficient than that for the thick ceramic layers under three-point and four-point bending loading, and the damage of the ceramic layer systems is faster under three-point bending than under four-point bending, resulted from different crack distributions, damage localization degrees, and energy dissipation. Moreover, the damage is slower for the nanostructured ceramic layers with the stronger interface strength or toughness between two layers. |
| 分类号 | 二类/Q1 |
| URL标识 | 查看原文 |
| WOS关键词 | THERMAL BARRIER COATINGS ; ACOUSTIC-EMISSION ; EVOLUTION ; DELAMINATION ; FAILURE ; CRACKING ; ENERGY ; MODEL ; SIMULATION ; TENSION |
| WOS研究方向 | Mechanics |
| 语种 | 英语 |
| WOS记录号 | WOS:000443279500043 |
| 资助机构 | NSFC grants of China [11672296, 11372318, 11432014, 11672301, 11521202] ; Strategic Priority Research Program of the Chinese Academy of Sciences [XDB22040501] |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/77847]  |
| 专题 | 力学研究所_非线性力学国家重点实验室 |
| 作者单位 | 1.[Liang, L. H. 2.Long, H.] Chinese Acad Sci, Inst Mech, LNM, Beijing 100190, Peoples R China 3.[Liu, H. Y. 4.Wei, Y. G.] Peking Univ, Coll Engn, Beijing 100871, Peoples R China 5.[Liang, L. H. 6.Long, H.] Univ Chinese Acad Sci, Beijing 101408, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liang LH,Liu HY,Long H,et al. Size-dependent damage and fracture of two-layer systems[J]. ENGINEERING FRACTURE MECHANICS,2018,199:635-646. |
| APA | 梁立红,Liu HY,Long H,&魏悦广.(2018).Size-dependent damage and fracture of two-layer systems.ENGINEERING FRACTURE MECHANICS,199,635-646. |
| MLA | 梁立红,et al."Size-dependent damage and fracture of two-layer systems".ENGINEERING FRACTURE MECHANICS 199(2018):635-646. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。