Microstructure and Properties of ZL101 Alloy Affected by Substrate Movement Speed of a Novel Semisolid Continuous Micro Fused-Casting for Metal Process
文献类型：期刊论文
| 作者 | Luo XQ(罗晓强); Han YJ; Li QB; Hu XM; Xue LW |
| 刊名 | JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION
 |
| 出版日期 | 2018-06-01 |
| 卷号 | 33期号:3页码:715-719 |
| 关键词 | micro fused-casting ZL101 alloy semisolid substrate movement speed additive manufacturing |
| ISSN号 | 1000-2413 |
| DOI | 10.1007/s11595-018-1883-z |
| 英文摘要 | A novel semisolid continuous Micro Fused-Casting additive manufacturing technology for producing a ZL101 alloy strip was developed, Micro Fused-Casting means that the semisolid metal slurry was pressed out from the outlet of bottom of crucible to the movable plate. The degree of sub-cooling was easily provided by movement of substrate in the micro fused-casting area. Under the aid of 3D manufacturing software, the ZL101 alloy strip was solidified and formed layer by layer. The microstructure and properties of ZL101 semisolid slurry were improved by the cooling conditions. The results showed that the ZL101 alloy strip samples fabricated by Micro Fused-Casting had uniform structures and good performances with the substrate movement speed at 20 mm/s and the temperature at 590., the ultimate tensile strength and elongation of the ZL101 alloy strip reached 242.59 MPa and 7.71%, while the average Vickers hardness was 82.55 HV. |
| 分类号 | Q4 |
| URL标识 | 查看原文 |
| WOS关键词 | STATE |
| WOS研究方向 | Materials Science, Multidisciplinary |
| 语种 | 英语 |
| WOS记录号 | WOS:000442018200030 |
| 资助机构 | National Natural Science Foundation of China [51341009] |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/77908]  |
| 专题 | 力学研究所_先进制造工艺力学重点实验室 |
| 作者单位 | 1.Pingdingshan Univ, Pingdingshan 467000, Peoples R China 2.Chinese Acad Sci, Inst Mech, Beijing 100190, Peoples R China |
| 推荐引用方式 GB/T 7714 | Luo XQ,Han YJ,Li QB,et al. Microstructure and Properties of ZL101 Alloy Affected by Substrate Movement Speed of a Novel Semisolid Continuous Micro Fused-Casting for Metal Process[J]. JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION,2018,33(3):715-719. |
| APA | 罗晓强,Han YJ,Li QB,Hu XM,&Xue LW.(2018).Microstructure and Properties of ZL101 Alloy Affected by Substrate Movement Speed of a Novel Semisolid Continuous Micro Fused-Casting for Metal Process.JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION,33(3),715-719. |
| MLA | 罗晓强,et al."Microstructure and Properties of ZL101 Alloy Affected by Substrate Movement Speed of a Novel Semisolid Continuous Micro Fused-Casting for Metal Process".JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION 33.3(2018):715-719. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。