Effects of Cr and Zr additions on microstructure and properties of Cu-Ni-Si alloys
文献类型：期刊论文
| 作者 | Wang, W; Kang, HJ; Chen, ZN; Chen, ZJ; Zou, CL; Li, RG; Yin, GM; Wang, TM; Chen ZJ(陈中军)
|
| 刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
 |
| 出版日期 | 2016 |
| 卷号 | 673页码:378-390 |
| 关键词 | Cu-Ni-Si alloy High strength High electrical conductivity Ageing Precipitation kinetics |
| DOI | 10.1016/j.msea.2016.07.021 |
| 英文摘要 | Cu-Ni-Si alloys are widely used for electrical applications owing to high strength and high electrical conductivity. In this work, the effects of Cr and Zr additions on microstructure and properties of Cu-Ni-Si alloys were investigated. The addition of Cr and Zr results in formation of Cr3Si and Ni2SiZr intermetallic compounds, respectively, thus increases the electrical conductivity of Cu-Ni-Si alloy and refines the microstructure. Microstructure analysis confirms the presence of delta-Ni2Si precipitates, which strengthens the alloy through Orowan mechanism. Alloying with Zr element deteriorates the mechanical property of Cu-Ni-Si alloy, whereas in the presence of Cr, to the contrary, the ultimate tensile strength is increased, whether Zr is incorporated or not. Moreover, the addition of Zr can decrease the stacking fault energy (SFE) and promote formation of deformation twins. The best integrated, performance is obtained through co-addition of Cr and Zr elements. The ultimate strength, elongation and electrical conductivity are 706 MPa, 9.5% and 48.2% IACS, respectively. The precipitation kinetics was discussed in terms of Avrami equation and the activation energy of Ni2Si precipitation was obtained. The calculated activation energies of precipitation are 105, 89, 115 and 111 kJ/mol for Cu-Ni-Si, Cu-Ni-Si-Zr, Cu-Ni-Si-Cr and Cu-Ni-Si-Cr-Zr alloy, respectively. (C) 2016 Elsevier B.V. All rights reserved. |
| 语种 | 英语 |
| WOS记录号 | WOS:000382410000043 |
| 源URL | [http://ir.ihep.ac.cn/handle/311005/260281]  |
| 专题 | 高能物理研究所_多学科研究中心 |
| 作者单位 | 中国科学院高能物理研究所 |
| 推荐引用方式 GB/T 7714 | Wang, W,Kang, HJ,Chen, ZN,et al. Effects of Cr and Zr additions on microstructure and properties of Cu-Ni-Si alloys[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2016,673:378-390. |
| APA | Wang, W.,Kang, HJ.,Chen, ZN.,Chen, ZJ.,Zou, CL.,...&陈中军.(2016).Effects of Cr and Zr additions on microstructure and properties of Cu-Ni-Si alloys.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,673,378-390. |
| MLA | Wang, W,et al."Effects of Cr and Zr additions on microstructure and properties of Cu-Ni-Si alloys".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 673(2016):378-390. |
入库方式： OAI收割
来源：高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。