Synthesis of ordered mesoporous uranium dioxide by a nanocasting route
文献类型：期刊论文
| 作者 | Wang L(王琳) ; Chai, ZF; Shi WQ(石伟群); Shi, WQ; Zhao, R; Wang, L; Chai ZF(柴之芳); Zhao R(赵然)
|
| 刊名 | RADIOCHIMICA ACTA
 |
| 出版日期 | 2016 |
| 卷号 | 104期号:8页码:549 |
| 关键词 | Porous materials phase transformation uranium dioxide nanocasting |
| DOI | 10.1515/ract-2015-2563 |
| 通讯作者 | 石伟群 |
| 英文摘要 | Ordered mesoporous UO2 with 3-D structure (for UO2-KIT-6) and nanowire bundles (for UO2-SBA-15) was synthesized for the first time by a nanocasting route using different ordered mesoporous silica (KIT-6 and SBA-15, respectively) as templates and uranyl nitrate hexahydrate as the metal precursor. The uranyl nitrate was impregnated into the mesopore of the silica template and was converted to U3O8 after the first step. The synthesis of ordered UO2 mesostructure was achieved by reducing the mesoporous U3O8 with silica composites under 5% H-2/Ar atmosphere at 700 degrees C, followed by a template removal process. The as-prepared UO2-KIT-6 had a particle size of several millimeters, and was constructed with uncoupled subframework mesostructure and crystalline walls, while UO2-SBA-15 possessed a rope-like morphology and consisted of nanowire arrays. The surface area and pore volume of ordered UO2 mesostructure are 47.2m(2) g(-1) and 0.23 cm(3) g(-1) for the UO2-KIT-6, and 54.4m(2) g(-1) and 0.28 cm(3) g(-1) for the UO2-SBA-15, respectively. |
| 语种 | 英语 |
| WOS记录号 | WOS:000381017600004 |
| 源URL | [http://ir.ihep.ac.cn/handle/311005/261103]  |
| 专题 | 高能物理研究所_院士 高能物理研究所_多学科研究中心 |
| 作者单位 | 中国科学院高能物理研究所 |
| 推荐引用方式 GB/T 7714 | Wang L,Chai, ZF,Shi WQ,et al. Synthesis of ordered mesoporous uranium dioxide by a nanocasting route[J]. RADIOCHIMICA ACTA,2016,104(8):549. |
| APA | 王琳.,Chai, ZF.,石伟群.,Shi, WQ.,Zhao, R.,...&赵然.(2016).Synthesis of ordered mesoporous uranium dioxide by a nanocasting route.RADIOCHIMICA ACTA,104(8),549. |
| MLA | 王琳,et al."Synthesis of ordered mesoporous uranium dioxide by a nanocasting route".RADIOCHIMICA ACTA 104.8(2016):549. |
入库方式： OAI收割
来源：高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。