Polyborosilazane preceramic as matrix resin of high temperature adhesive for graphite bonding
文献类型：期刊论文
| 作者 | Li, Shuqin1; Luo, Yongming2; Wang, Linhao2; Xu, Caihong2 |
| 刊名 | INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY
 |
| 出版日期 | 2017-09-01 |
| 卷号 | 14期号:5页码:999-1005 |
| 关键词 | Heat Treatment High Temperature Adhesives Joining Mechanical Properties Of Adhesives |
| 英文摘要 | In this study, a modified high temperature adhesive based on polyborosilazane preceramic was developed for joining graphite. The properties of adhesive as well as bonding performance of both directly cured joints and calcined joints were investigated. The results showed that the shear strength reached the highest value 13.6MPa after calcination at 1100 degrees C due to the formation of heat-resistant ceramic phases and solidification of molten species during joining process. Besides, the compressive shear strength of cured adhesive without posttreatment was kept above 6MPa during test from RT to 1100 degrees C, which made it possible applied directly in practical high temperature environment. |
| 语种 | 英语 |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/39258]  |
| 专题 | 化学研究所_高技术材料实验室 |
| 作者单位 | 1.China Aerosp Sci & Ind Corp, Inst 306, Beijing, Peoples R China 2.Chinese Acad Sci, Inst Chem, Beijing, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li, Shuqin,Luo, Yongming,Wang, Linhao,et al. Polyborosilazane preceramic as matrix resin of high temperature adhesive for graphite bonding[J]. INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,2017,14(5):999-1005. |
| APA | Li, Shuqin,Luo, Yongming,Wang, Linhao,&Xu, Caihong.(2017).Polyborosilazane preceramic as matrix resin of high temperature adhesive for graphite bonding.INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,14(5),999-1005. |
| MLA | Li, Shuqin,et al."Polyborosilazane preceramic as matrix resin of high temperature adhesive for graphite bonding".INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY 14.5(2017):999-1005. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。