Fabrication of methylammonium bismuth iodide through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers
文献类型：期刊论文
| 作者 | Wang, Huijia1,2; Tian, Jianhua1; Jiang, Kejian2; Zhang, Yu1,2; Fan, Haochen2; Huang, Jinhua2; Yang, Lian-ming2; Guan, Bo2; Song, Yanlin2 |
| 刊名 | RSC ADVANCES
 |
| 出版日期 | 2017 |
| 卷号 | 7期号:69页码:43826-43830 |
| 英文摘要 | Methylammonium bismuth iodide (MA(3)Bi(2)I(9)) perovskite, has been deposited on a mesoporous TiO2 film with high homogeneousity and coverage through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers, resulting in higher power conversion efficiency in the perovskite solar cell as compared with that prepared using a conventional one-step solution method. |
| 语种 | 英语 |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/41051]  |
| 专题 | 化学研究所_绿色印刷实验室 |
| 作者单位 | 1.Tianjin Univ, Sch Chem Engn & Technol, Tianjin 300072, Peoples R China 2.Chinese Acad Sci, Inst Chem, Key Lab Green Printing, Beijing 100190, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang, Huijia,Tian, Jianhua,Jiang, Kejian,et al. Fabrication of methylammonium bismuth iodide through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers[J]. RSC ADVANCES,2017,7(69):43826-43830. |
| APA | Wang, Huijia.,Tian, Jianhua.,Jiang, Kejian.,Zhang, Yu.,Fan, Haochen.,...&Song, Yanlin.(2017).Fabrication of methylammonium bismuth iodide through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers.RSC ADVANCES,7(69),43826-43830. |
| MLA | Wang, Huijia,et al."Fabrication of methylammonium bismuth iodide through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers".RSC ADVANCES 7.69(2017):43826-43830. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。