Superhydrophilic Antireflective Periodic Mesoporous Organosilica Coating on Flexible Polyimide Substrate with Strong Abrasion Resistance

文献类型:期刊论文

作者Wang, J; Zhang, C; Yang, CM; Zhang, C; Wang, MC; Zhang, J; Xu, Y
刊名ACS APPLIED MATERIALS & INTERFACES
出版日期2017
卷号9期号:6页码:5468-5476
关键词Antireflective Pmo Coating Superhydrophilic Polyimide Abrasion-resistance
ISSN号1944-8244
DOI10.1021/acsami.6b14117
文献子类期刊论文
英文摘要Superhydrophilic antireflective periodic mesoporous organosilica (PMO) coating was prepared on flexible polyimide substrate via solvent evaporation-induced self-assembly (SEISM method, in which tetraethoxysilane (TEOS) and a special bridged silsesquioxane were used as reactants. The bridged silsesquioxane, EG-BSQ was synthesized through the stoichiometric reaction between 3-glycidoxyporpyltrimethoxysilane (GPTMS) and ethylene diamine (EDA). Under the influence of surfactant, TEOS and EG-BSQ co-condensed and enclosed the ordered mesporous in the coating. The results of grazing-incidence small-angle X-ray scattering (GISAXS) and the transmission electron microscope (TEM) indicated that the mesopores belonged to a Fmmm orthorhombic symmetry structure. With increasing EG-BSQ concentration, the mesoporous structure in the PMO coating becomes more and more disordered because silica mesopore walls shrunk or collapsed during calcination and consequently the refractive index of PMO coating became larger. The antireflective (AR) PMO coating showed an optical transmittance of 99.54% on polyimide (PI) much higher than the 88.68% of bare PI. The water contact angle of PMO coating was less than 9.0, which indicated the AR PMO coating was superhydrophilic. Moreover, the PMO coating showed an excellent mechanical property, the transmittance of the PMO coating displayed a very low loss of 0.1% after abrasion of 25 cycles by CS-10F wearaser.
语种英语
WOS记录号WOS:000394481800048
源URL[http://ir.sinap.ac.cn/handle/331007/27459]  
专题上海应用物理研究所_中科院上海应用物理研究所2011-2017年
推荐引用方式
GB/T 7714
Wang, J,Zhang, C,Yang, CM,et al. Superhydrophilic Antireflective Periodic Mesoporous Organosilica Coating on Flexible Polyimide Substrate with Strong Abrasion Resistance[J]. ACS APPLIED MATERIALS & INTERFACES,2017,9(6):5468-5476.
APA Wang, J.,Zhang, C.,Yang, CM.,Zhang, C.,Wang, MC.,...&Xu, Y.(2017).Superhydrophilic Antireflective Periodic Mesoporous Organosilica Coating on Flexible Polyimide Substrate with Strong Abrasion Resistance.ACS APPLIED MATERIALS & INTERFACES,9(6),5468-5476.
MLA Wang, J,et al."Superhydrophilic Antireflective Periodic Mesoporous Organosilica Coating on Flexible Polyimide Substrate with Strong Abrasion Resistance".ACS APPLIED MATERIALS & INTERFACES 9.6(2017):5468-5476.

入库方式: OAI收割

来源:上海应用物理研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。