Effect of Mg on the Microstructure and Corrosion Resistance of the Continuously Hot-Dip Galvanizing Zn-Mg Coating
文献类型：期刊论文
| 作者 | Dong, AP; Li, BP; Lu, YL; Zhu, GL; Xing, H; Shu, D; Sun, BD; Wang, J |
| 刊名 | MATERIALS
 |
| 出版日期 | 2017 |
| 卷号 | 10期号:8页码:- |
| 关键词 | Coated Steel Sheet Zinc Behavior Alloys |
| ISSN号 | 1996-1944 |
| DOI | 10.3390/ma10080980 |
| 文献子类 | 期刊论文 |
| 英文摘要 | The microstructure of continuously hot-dip galvanizing Zn-Mg coating was investigated in order to obtain the mechanism of the effects of Mg on the corrosion resistance. In this paper, the vertical section of the Zn-0.20 wt % Al-Mg ternary phase diagram near the Al-low corner was calculated. The results indicates that the phase composition of the Zn-0.20 wt % Al-Mg ternary phase diagram near the Al-low corner is the same as Zn-Mg binary phase diagram, suggesting Al in the Zn-Mg (ZM) coatings mainly concentrates on the interfacial layer between the coating and steel substrate. The microstructure of continuously hot-dip galvanizing ZM coatings with 0.20 wt % Al containing 1.0-3.0 wt % Mg was investigated using tunneling electron microscopy (TEM). The morphology of Zn in the coating changes from bulk to strip and finally to mesh-like, and the MgZn2 changes from rod-like to mesh-like with the Mg content increasing. Al in the ZM coatings mainly segregates at the Fe2Al5 inhibition layer and the Mg added to the Zn bath makes this inhibition layer thinner and uneven. Compared to GI coating, the time of the first red rust appears increases by more than two-fold and expansion rate of red rust reduces by more than four-fold in terms of salt spray experiment. The ZM coating containing 2.0 wt % Mg has the best corrosion resistance. The enhanced corrosion resistance of ZM coatings mainly depends on different corrosion products. |
| WOS关键词 | COATED STEEL SHEET ; ZINC ; BEHAVIOR ; ALLOYS |
| 语种 | 英语 |
| WOS记录号 | WOS:000408731600134 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/28626]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Dong, AP,Li, BP,Lu, YL,et al. Effect of Mg on the Microstructure and Corrosion Resistance of the Continuously Hot-Dip Galvanizing Zn-Mg Coating[J]. MATERIALS,2017,10(8):-. |
| APA | Dong, AP.,Li, BP.,Lu, YL.,Zhu, GL.,Xing, H.,...&Wang, J.(2017).Effect of Mg on the Microstructure and Corrosion Resistance of the Continuously Hot-Dip Galvanizing Zn-Mg Coating.MATERIALS,10(8),-. |
| MLA | Dong, AP,et al."Effect of Mg on the Microstructure and Corrosion Resistance of the Continuously Hot-Dip Galvanizing Zn-Mg Coating".MATERIALS 10.8(2017):-. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。