Fluorine gradient-doped LiNi0.5Mn1.5O4 spinel with improved high voltage stability for Li-ion batteries
文献类型：期刊论文
| 作者 | Luo, Y; Li, HY; Lu, TL; Zhang, YX; Mao, SS; Liu, Z; Wen, W; Xie, JY; Yan, LQ |
| 刊名 | ELECTROCHIMICA ACTA
 |
| 出版日期 | 2017 |
| 卷号 | 238期号:-页码:237-245 |
| 关键词 | Electrochemical Performance Cathode Material Thermal-stability Surface Modification Limn1.5ni0.5-xmxo4 m Rate Capability Lithium Cation Electrodes Fe |
| ISSN号 | 0013-4686 |
| DOI | 10.1016/j.electacta.2017.04.043 |
| 文献子类 | 期刊论文 |
| 英文摘要 | The fluorine gradient-doped LiNi0.5Mn1.5O4 spinels are synthesized by a facile one-step method and the effect of heat treatment on their structure, morphology, and electrochemical performance are investigated. The results show that introduction of fluorine leads to a larger lattice parameter and particle size, and the formation of F-enriched surface. Whereas at 400 degrees C, the fluorine gradient-doped LiNi0.5Mn1.5O4 sample exhibits an improved long-term cycling stability and high rate performance, due to` the suppression of the reaction between electrolyte and cathode, resulting in a decrease in the total resistance and the formation of a thin, uniform and smooth film on the surface. As a result of in situ XRD with charged pristine and the fluorine gradient-doped samples, the similar thermal-decomposition pathways from the charged spinel to the final NiMn2O4-type spinel structure with a small amount of NiMnO3 and alpha-Mn2O3 are observed. In addition, the disappearance temperature of the charged spinel structures is at about 280 degrees C for the fluorine gradient-doped sample, exhibiting an improved thermal stability of high voltage cathode material. These results show that fluorine gradient-doped LiNi0.5Mn1.5O4 sample is a promising positive electrode material for high performance lithium ion batteries. (C) 2017 Elsevier Ltd. All rights reserved. |
| WOS关键词 | ELECTROCHEMICAL PERFORMANCE ; CATHODE MATERIAL ; THERMAL-STABILITY ; SURFACE MODIFICATION ; LIMN1.5NI0.5-XMXO4 M ; RATE CAPABILITY ; LITHIUM ; CATION ; ELECTRODES ; FE |
| 语种 | 英语 |
| WOS记录号 | WOS:000401113500027 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/28661]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Luo, Y,Li, HY,Lu, TL,et al. Fluorine gradient-doped LiNi0.5Mn1.5O4 spinel with improved high voltage stability for Li-ion batteries[J]. ELECTROCHIMICA ACTA,2017,238(-):237-245. |
| APA | Luo, Y.,Li, HY.,Lu, TL.,Zhang, YX.,Mao, SS.,...&Yan, LQ.(2017).Fluorine gradient-doped LiNi0.5Mn1.5O4 spinel with improved high voltage stability for Li-ion batteries.ELECTROCHIMICA ACTA,238(-),237-245. |
| MLA | Luo, Y,et al."Fluorine gradient-doped LiNi0.5Mn1.5O4 spinel with improved high voltage stability for Li-ion batteries".ELECTROCHIMICA ACTA 238.-(2017):237-245. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。