Microstructure and Mechanical Properties of Fiber Laser Welded GH3535 Superalloy
文献类型：期刊论文
| 作者 | Yu, K; Jiang, ZG; Li, CW; Chen, SJ; Tao, W; Zhou, XT; Li, ZJ |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2017 |
| 卷号 | 33期号:11页码:1289-1299 |
| 关键词 | Mo-cr Superalloy Heat-affected Zone Fusion Zone Thermal Cycle Temperature Cracking Carbide Metal |
| ISSN号 | 1005-0302 |
| DOI | 10.1016/j.jmst.2016.11.026 |
| 文献子类 | 期刊论文 |
| 英文摘要 | As a primary material of the thorium molten salt reactor (TMSR) that is a suitable candidate reactor the Generation IV nuclear reactors, GH3535 superalloy was successfully welded. The effect of laser beam welding (LBW) on microstructure evolution of fusion zone (FZ) and heat affected zone (HAZ), such as element segregation, precipitate behavior and grain evolution, was investigated. The microhardness and tensile properties were tested and discussed. The results of microstructure evolution showed that a number of fine M6C-gamma eutectic phases precipitated at solidification grain boundaries and interdendritic region in FZ. Compared to base metal zone (BMZ), the grain size of HAZ has no obvious change. While a few of M6C-gamma eutectic phases were observed in partially melted zone (PMZ) of HAZ. The results of microhardness indicated that the hardness of FZ was higher than that of HAZ and BMZ. The results of tensile test showed that the ultimate tensile strength of joints at room temperature, 650 and 700 degrees C were 98%, 97% and 99% of that of BM, respectively. All the tensile specimens of joints failed in BMZ rather than in PMZ where M6C carbides had been transformed into M6C-gamma eutectic phases. (C) 2016 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| WOS关键词 | MO-CR SUPERALLOY ; HEAT-AFFECTED ZONE ; FUSION ZONE ; THERMAL CYCLE ; TEMPERATURE ; CRACKING ; CARBIDE ; METAL |
| 语种 | 英语 |
| WOS记录号 | WOS:000416994500009 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/28734]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Yu, K,Jiang, ZG,Li, CW,et al. Microstructure and Mechanical Properties of Fiber Laser Welded GH3535 Superalloy[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2017,33(11):1289-1299. |
| APA | Yu, K.,Jiang, ZG.,Li, CW.,Chen, SJ.,Tao, W.,...&Li, ZJ.(2017).Microstructure and Mechanical Properties of Fiber Laser Welded GH3535 Superalloy.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,33(11),1289-1299. |
| MLA | Yu, K,et al."Microstructure and Mechanical Properties of Fiber Laser Welded GH3535 Superalloy".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 33.11(2017):1289-1299. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。