Evolution of carbide precipitates in Hastelloy N joints during welding and post weld heat treatment
文献类型：期刊论文
| 作者 | Wang, WX; Li, CW; Jiang, L; Ye, XX; Yu, K; Chen, SJ; Li, ZJ; Zhou, XT |
| 刊名 | MATERIALS CHARACTERIZATION
 |
| 出版日期 | 2018 |
| 卷号 | 135页码:311-316 |
| 关键词 | Mo-cr Superalloy Term Thermal Exposure Affected Zone Mechanical-properties Gh3535 Superalloy M6c Carbide Microstructure Steel Alloy Temperature |
| ISSN号 | 1044-5803 |
| DOI | 10.1016/j.matchar.2017.11.045 |
| 文献子类 | 期刊论文 |
| 英文摘要 | The effects of welding and post weld heat treatment (PWHT) on the morphology, composition and lattice parameter of the precipitates in the welding joints of Hastelloy N alloy have been investigated. Joint samples were prepared using a gas tungsten arc welding process with ERNiMo-2 fillers, and then solid-solution treated at 1100 degrees C for 20 min. After welding, eutectic M6C carbides can be observed in the heat affected zones (HAZ) and weld zones (WZ). These eutectic M6C carbides become spheroidized during the following PWHT. The concentration of Si decreases during the transformation from the primary ones to eutectic ones, and then increases during the spheroidizing process. The total concentration of Si + Cr in M6C carbides remains stable during welding and PWHT. At the same time, the heat leads to the outward diffusion of Mo from the M6C carbides, which results in a decrease of the lattice parameter. |
| 语种 | 英语 |
| WOS记录号 | WOS:000423248200037 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/29009]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 作者单位 | 1.Wang, WX 2.Li, CW 3.Jiang, L 4.Ye, XX 5.Yu, K 6.Chen, SJ 7.Li, ZJ 8.Zhou, XT |
| 推荐引用方式 GB/T 7714 | Wang, WX,Li, CW,Jiang, L,et al. Evolution of carbide precipitates in Hastelloy N joints during welding and post weld heat treatment[J]. MATERIALS CHARACTERIZATION,2018,135:311-316. |
| APA | Wang, WX.,Li, CW.,Jiang, L.,Ye, XX.,Yu, K.,...&Zhou, XT.(2018).Evolution of carbide precipitates in Hastelloy N joints during welding and post weld heat treatment.MATERIALS CHARACTERIZATION,135,311-316. |
| MLA | Wang, WX,et al."Evolution of carbide precipitates in Hastelloy N joints during welding and post weld heat treatment".MATERIALS CHARACTERIZATION 135(2018):311-316. |