An excellent cyan-emitting orthosilicate phosphor for NUV-pumped white LED application
文献类型：期刊论文
| 作者 | Liu, Y. F.; J. Silver; R. J. Xie; J. H. Zhang; H. W. Xu; H. Z. Shao; J. Jiang and H. C. Jiang |
| 刊名 | Journal of Materials Chemistry C
 |
| 出版日期 | 2017 |
| 卷号 | 5期号:47 |
| 英文摘要 | In this paper, a cyan-emitting phosphor BLS:Ce3+ is reported that has a broad emission band covering both the blue and green regions of the visible spectrum, which can be used instead of two separate blue and green phosphors. The excitation peak of BLS:Ce3+ is located at 400 nm, which matches well with the emission light of efficient near-ultraviolet (NUV) chips. The BLS:Ce3+ phosphor has an internal quantum efficiency (IQE) higher than 90% at room temperature (RT) and an excellent thermal stability (a small reduction of 3% at 150 degrees C relative to the IQE at RT) and is environmentally robust (a small degradation of 6% occurs after aging for 1600 h at 85 degrees C/85% RH relative to the room-temperature IQE value). Using the BLS:Ce3+ phosphor, coupled only with a CaAlSiN3:Eu2+ red phosphor and a 395 nm NUV chip, a NUV-based WLED with a high color rendering index of 90.6 has been achieved. Moreover, the luminous efficiency reaches as high as 32.2 lm W-1, which is much better than that of the NUV-WLEDs employing three phosphors (blue, green and red). |
| 语种 | 英语 |
| WOS记录号 | WOS:000417284100009 |
| 源URL | [http://ir.ciomp.ac.cn/handle/181722/59106]  |
| 专题 | 长春光学精密机械与物理研究所_中科院长春光机所知识产出 |
| 推荐引用方式 GB/T 7714 | Liu, Y. F.,J. Silver,R. J. Xie,et al. An excellent cyan-emitting orthosilicate phosphor for NUV-pumped white LED application[J]. Journal of Materials Chemistry C,2017,5(47). |
| APA | Liu, Y. F..,J. Silver.,R. J. Xie.,J. H. Zhang.,H. W. Xu.,...&J. Jiang and H. C. Jiang.(2017).An excellent cyan-emitting orthosilicate phosphor for NUV-pumped white LED application.Journal of Materials Chemistry C,5(47). |
| MLA | Liu, Y. F.,et al."An excellent cyan-emitting orthosilicate phosphor for NUV-pumped white LED application".Journal of Materials Chemistry C 5.47(2017). |
入库方式： OAI收割
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。