Luminescence properties and its red shift of blue-emitting phosphor Na3YSi3O9:Ce3+ for UV LED
文献类型：期刊论文
| 作者 | Wang, F.; W. R. Wang; L. L. Zhang; J. J. Zheng; Y. Jin and J. H. Zhang |
| 刊名 | Rsc Advances
 |
| 出版日期 | 2017 |
| 卷号 | 7期号:44 |
| 英文摘要 | A series of Na3YSi3O9:Ce3+ phosphors have been synthesized via a conventional high temperature solidstate reaction. Each crystal structure was characterized by X-ray diffraction (XRD) and refined by the Rietveld method. Luminescence properties of Na3YSi3O9:Ce3+ phosphors such as emission red shifts, fluorescence decay curves, thermal stability, and CIE values were systematically investigated. Upon 300 nm excitation, the emission peaks of Na3YSi3O9:Ce3+ phosphors red shift from 385 nm to 415 nm with Ce3+ concentration increasing from 0.002 to 0.11. Moreover, this red-shift phenomenon also occurs with an excitation wavelength from 270 nm to 340 nm as the Ce3+ concentration determined, which has been explained using the centroid shift and crystal field splitting. The quenching concentration of Ce3+ in the host Na3YSi3O9 is determined to be about 3 mol% and the critical distance is calculated to be about 16.623 angstrom. The energy dispersion mechanism between Ce3+ ions was verified to be a dipole-dipole interaction. Temperature-dependent luminescence of Na3YSi3O9:0.03Ce(3+) from 25 degrees C to 250 degrees C was evaluated, and the corresponding activation energy Delta E is 0.277 eV. Not only crystal field splitting but also centroid shift plays an important role in the red-shift of the Na3YSi3O9:Ce3+ phosphors, which may contribute to future research in designing novel solid phosphors by modifying composition of the host lattice to affect crystal field splitting and centroid shift, and then adjusting emission wavelengths to match the purposed application. |
| 语种 | 英语 |
| 源URL | [http://ir.ciomp.ac.cn/handle/181722/59245]  |
| 专题 | 长春光学精密机械与物理研究所_中科院长春光机所知识产出 |
| 推荐引用方式 GB/T 7714 | Wang, F.,W. R. Wang,L. L. Zhang,et al. Luminescence properties and its red shift of blue-emitting phosphor Na3YSi3O9:Ce3+ for UV LED[J]. Rsc Advances,2017,7(44). |
| APA | Wang, F.,W. R. Wang,L. L. Zhang,J. J. Zheng,&Y. Jin and J. H. Zhang.(2017).Luminescence properties and its red shift of blue-emitting phosphor Na3YSi3O9:Ce3+ for UV LED.Rsc Advances,7(44). |
| MLA | Wang, F.,et al."Luminescence properties and its red shift of blue-emitting phosphor Na3YSi3O9:Ce3+ for UV LED".Rsc Advances 7.44(2017). |
入库方式： OAI收割
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。