Low temperature-sintering and microstructure of highly transparent yttria ceramics
文献类型：期刊论文
| 作者 | Zhang, Le; Ben, Yue; Chen, Hao; Tang, Dingyuan; Fu, Xianzhu; Sun, Rong; Song, Bo; Wong, Chingping |
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2017 |
| 文献子类 | 期刊论文 |
| 英文摘要 | Highly transparent yttria ceramics were successfully fabricated by vacuum pre-sintering and post hot isostatic pressing (HIP) treatment both under very lowtemperatures synthesized from powders by a co-precipitated method. The morphologies and microstructures, density and thermal mechanical changes, and optical properties of ceramics under different processing stages were systematically characterized by (F) SEM, TMA, optical microscope and UV-Vis-IR spectrophotometer, respectively. The full densification of yttria ceramics could be achieved just at as low as 1450 degrees C for 4 h (vacuum pre-sintering) and 1400 degrees C for 3 h (post-HIP). The fabricated ceramics exhibited a uniform and fine microstructure and high optical performance. The average grain size was as small as 0.74 mm. The in-line transmittance reached 81.7% at 1100 nm (1 mm thickness). The transparent yttria ceramics were attractive without any sintering additives at such low pre-sintering and post-HIP temperatures. |
| URL标识 | 查看原文 |
| 语种 | 英语 |
| 源URL | [http://ir.siat.ac.cn:8080/handle/172644/11665]  |
| 专题 | 深圳先进技术研究院_集成所 |
| 作者单位 | JOURNAL OF ALLOYS AND COMPOUNDS |
| 推荐引用方式 GB/T 7714 | Zhang, Le,Ben, Yue,Chen, Hao,et al. Low temperature-sintering and microstructure of highly transparent yttria ceramics[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2017. |
| APA | Zhang, Le.,Ben, Yue.,Chen, Hao.,Tang, Dingyuan.,Fu, Xianzhu.,...&Wong, Chingping.(2017).Low temperature-sintering and microstructure of highly transparent yttria ceramics.JOURNAL OF ALLOYS AND COMPOUNDS. |
| MLA | Zhang, Le,et al."Low temperature-sintering and microstructure of highly transparent yttria ceramics".JOURNAL OF ALLOYS AND COMPOUNDS (2017). |
入库方式： OAI收割
来源：深圳先进技术研究院
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。