Hot corrosion of Ni, Cr, and 80Ni20Cr in the presence of NaCl and water vapor at 750 degrees C
文献类型：期刊论文
| 作者 | Chen, L. Y.1,2; Lan, H.2; Huang, C. B.2; Yang, B.1,3; Du, L. Z.2; Zhang, W. G.2 |
| 刊名 | MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
 |
| 出版日期 | 2017-11-01 |
| 卷号 | 68期号:11页码:1172-1179 |
| 关键词 | Hot Corrosion Nacl Synergistic Effect Water Vapor |
| ISSN号 | 0947-5117 |
| DOI | 10.1002/maco.201709513 |
| 文献子类 | Article |
| 英文摘要 | The hot corrosion of Ni, Cr, and 80Ni20Cr in the presence of NaCl and water vapor at 750 degrees C was studied. The results indicated that no significant oxidation or corrosion effect of Ni was found in this case. However, a severe damage caused by the synergistic effect of NaCl deposit and water vapor on Cr was found. Both theoretical and experimental results have shown that Cr could react with NaCl or water vapor and form corrosive Cl-2 or HCl, accelerating the corrosion of Cr by chlorination and oxidation. The element Ni in 80Ni20Cr alloy was accelerated corroded by means of reactions among Cr and solid NaCl as well as water vapor. |
| WOS关键词 | Fe-cr ; Alloys ; Oxidation ; Superalloys ; Behavior ; Coatings ; Chromium ; Deposit |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000414634200002 |
| 资助机构 | National Natural Science Foundation of China(51471159 ; 51671180) |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/23382]  |
| 专题 | 过程工程研究所_多相复杂系统国家重点实验室 |
| 作者单位 | 1.Univ Sci & Technol Beijing, State Key Lab Adv Met & Mat, Beijing 100083, Peoples R China 2.Chinese Acad Sci, Inst Proc Engn, Lab Particle Sci & Engn, State Key Lab Multiphase Complex Syst, Beijing 100190, Peoples R China 3.Univ Sci & Technol Beijing, Collaborat Innovat Ctr Steel Technol, Beijing 100083, Peoples R China |
| 推荐引用方式 GB/T 7714 | Chen, L. Y.,Lan, H.,Huang, C. B.,et al. Hot corrosion of Ni, Cr, and 80Ni20Cr in the presence of NaCl and water vapor at 750 degrees C[J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,2017,68(11):1172-1179. |
| APA | Chen, L. Y.,Lan, H.,Huang, C. B.,Yang, B.,Du, L. Z.,&Zhang, W. G..(2017).Hot corrosion of Ni, Cr, and 80Ni20Cr in the presence of NaCl and water vapor at 750 degrees C.MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,68(11),1172-1179. |
| MLA | Chen, L. Y.,et al."Hot corrosion of Ni, Cr, and 80Ni20Cr in the presence of NaCl and water vapor at 750 degrees C".MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION 68.11(2017):1172-1179. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。