Corrosion behavior of low-Cr steel rebars in alkaline solutions with different pH in the presence of chlorides
文献类型：期刊论文
| 作者 | Liu, Ming; Cheng, Xuequn; Li, Xiaogang; Lu, Tian Jian |
| 刊名 | JOURNAL OF ELECTROANALYTICAL CHEMISTRY
 |
| 出版日期 | 2017 |
| 卷号 | 803页码:40-50 |
| ISSN号 | 1572-6657 |
| 英文摘要 | Corrosion behaviors of HRB400 carbon steel and three low-Cr steel rebars in alkaline solution simulating concrete pore solution with various pH and chlorides values were studied using cyclic voltammetry, potentiodynamic polarization, electrochemical impedance spectroscopy, and Mott-Schottky combined with scanning electron microscope as well as X-ray Diffraction. Results show that pH and chloride play important roles in the formation of passive films on steel rebars. As pH value decreased, the pitting potential shifts negatively, the polarization resistance decreases while the density of current carrier in the passive film increases. In the absence of chloride, stable passive film cannot form on carbon steel in simulated concrete pore solution with pH 9.6, Cr3+ cannot remain stable in the passive film on 3Cr and 5Cr steel, and passive film on low-Cr steels are more stable than that of carbon steel. While pitting corrosion is promoted by increasing chloride ions, Cr effectively reduces pitting propagation, resulting in the high passivation capability of steel rebar in carbonated concrete pore solution. The corrosion products of carbon and low-Cr steels have common characteristics, with Cr accelerating the formation of protective alpha-FeOOH and lowering the corrosion rate. Therefore, Cr-modified steel presents excellent passive behavior and pitting corrosion resistance in simulated carbonated concrete pore solution, which can be further enhanced by increasing the Cr content. |
| 公开日期 | 2017-12-25 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/13579]  |
| 专题 | 2017专题 |
| 推荐引用方式 GB/T 7714 | Liu, Ming,Cheng, Xuequn,Li, Xiaogang,et al. Corrosion behavior of low-Cr steel rebars in alkaline solutions with different pH in the presence of chlorides[J]. JOURNAL OF ELECTROANALYTICAL CHEMISTRY,2017,803:40-50. |
| APA | Liu, Ming,Cheng, Xuequn,Li, Xiaogang,&Lu, Tian Jian.(2017).Corrosion behavior of low-Cr steel rebars in alkaline solutions with different pH in the presence of chlorides.JOURNAL OF ELECTROANALYTICAL CHEMISTRY,803,40-50. |
| MLA | Liu, Ming,et al."Corrosion behavior of low-Cr steel rebars in alkaline solutions with different pH in the presence of chlorides".JOURNAL OF ELECTROANALYTICAL CHEMISTRY 803(2017):40-50. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。