In Situ TEM Study of Interaction between Dislocations and a Single Nanotwin under Nanoindentation
文献类型：期刊论文
| 作者 | Wang, Bo; Zhang, Zhenyu; Cui, Junfeng; Jiang, Nan; Lyu, Jilei; Chen, Guoxin; Wang, Jia; Liu, Zhiduo; Yu, Jinhong; Lin, Chengte |
| 刊名 | ACS APPLIED MATERIALS & INTERFACES
 |
| 出版日期 | 2017 |
| 卷号 | 9期号:35页码:29451-29456 |
| ISSN号 | 1944-8244 |
| 英文摘要 | Nanotwinned (nt) materials exhibit excellent mechanical properties, and have been attracting much more attention of late. Nevertheless, the fundamental mechanism of interaction between dislocations and a single nanotwin is not understood. In this study, in situ transmission electron microscopy (TEM) nanoindentation is performed, on a specimen-of a nickel (Ni) alloy containing a single nanotwin of 89 nm in thickness. The specimen is prepared using focused ion beam (BIB) technique from an nt surface, which is formed by a novel approach-tinder indentation using a developed diamond panel with tips array. The stiffness of the specimen is ten times that-of the pristine counterparts during loading. The ultrahigh stiffness is attributed, to the generation of nanotwins and the impediment of the single twin. to the dislocations. Two peak loads-are induced by the activation of a new slip system and the penetration of dislocations over the single nanotwin, respectively. One slip band is parallel to the single nanotwin, indicating the slip of dislocations along the nanotwin. In situ TEM observation of nanoindentation reveals a new insight for the interaction between dislocations and a single nanotwin. This paves the way for design and preparation of high-performance nt surfaces of Ni alloys used for aircraft engines, gas turbines, turbocharger components, ducts, and absorbers. |
| 公开日期 | 2017-12-25 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/13632]  |
| 专题 | 2017专题 |
| 推荐引用方式 GB/T 7714 | Wang, Bo,Zhang, Zhenyu,Cui, Junfeng,et al. In Situ TEM Study of Interaction between Dislocations and a Single Nanotwin under Nanoindentation[J]. ACS APPLIED MATERIALS & INTERFACES,2017,9(35):29451-29456. |
| APA | Wang, Bo.,Zhang, Zhenyu.,Cui, Junfeng.,Jiang, Nan.,Lyu, Jilei.,...&Guo, Dongming.(2017).In Situ TEM Study of Interaction between Dislocations and a Single Nanotwin under Nanoindentation.ACS APPLIED MATERIALS & INTERFACES,9(35),29451-29456. |
| MLA | Wang, Bo,et al."In Situ TEM Study of Interaction between Dislocations and a Single Nanotwin under Nanoindentation".ACS APPLIED MATERIALS & INTERFACES 9.35(2017):29451-29456. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。