Growth and characterization of large size undoped p-type SnSe single crystal by Horizontal Bridgman method
文献类型：期刊论文
| 作者 | Jin, Min; Shao, Hezhu; Hu, Haoyang; Li, Debo; Shen, Hui; Xu, Jiayue; Jiang, Jun |
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2017 |
| 卷号 | 712页码:857-862 |
| ISSN号 | 0925-8388 |
| 英文摘要 | A Horizontal Bridgman (HB) method was employed attempt to grow large size undoped SnSe single crystal. SnSe was crystallized under 2-3 degrees C/cm temperature gradient and cooled to room temperature at a rate of similar to 25 degrees C/h to release thermal stress. SnSe crystals grown from liquid solution and volatilized vapor were obtained simultaneously. Two single crystals with size about 30 x 20 x 15 mm(3) and 35 x 15 x 15 mm(3) were peeled off from the liquid growth SnSe, which were reported to be the largest so far. The as-grown SnSe single crystal had standard orthorhombic Pnma space group at room temperature. Stoichiometry ratio of the crystal was measured Sn: Se = 1:1. The density of as-grown crystal is similar to 6.16 g/ cm(3), which is very close to 100% of the theoretical value of SnSe. The obtained SnSe single crystal displayed p-type character with a carrier density of 5.1 x 10(17) cm(-3) at room temperature. Thermoelectric properties in directions parallel and perpendicular to cleavage be plane were analyzed, the maximum thermoelectric figure of merit ZT were ZT(||bc), = 1.1 and ZT(perpendicular to bc) = 0.24 near Pnma-Cmcm phase transition temperature. (C) 2017 Elsevier B.V. All rights reserved. |
| 公开日期 | 2017-12-25 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/13720]  |
| 专题 | 2017专题 |
| 推荐引用方式 GB/T 7714 | Jin, Min,Shao, Hezhu,Hu, Haoyang,et al. Growth and characterization of large size undoped p-type SnSe single crystal by Horizontal Bridgman method[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2017,712:857-862. |
| APA | Jin, Min.,Shao, Hezhu.,Hu, Haoyang.,Li, Debo.,Shen, Hui.,...&Jiang, Jun.(2017).Growth and characterization of large size undoped p-type SnSe single crystal by Horizontal Bridgman method.JOURNAL OF ALLOYS AND COMPOUNDS,712,857-862. |
| MLA | Jin, Min,et al."Growth and characterization of large size undoped p-type SnSe single crystal by Horizontal Bridgman method".JOURNAL OF ALLOYS AND COMPOUNDS 712(2017):857-862. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。