Direct formation of NaZn13-structure La(Fe,Si)(13) phase by directional solidification
文献类型：期刊论文
| 作者 | Yan, Aru; Shao, Yanyan; Liu, Jian; Zhang, Pengna |
| 刊名 | MATERIALS LETTERS
 |
| 出版日期 | 2017 |
| 卷号 | 193页码:34-37 |
| ISSN号 | 0167-577X |
| 英文摘要 | We have demonstrated that the La(Fe,Si)(13) magnetocaloric phase can be directly formed from molten on extremely slow cooling by the employment of directional solidification technique. A large amount of this magnetocaloric phase of about 85% was achieved in the as-solidified state with a cooling rate of 0.005 K/s. A large magnetic entropy change of 13.5 J/kg K under an applied field of 2 T was obtained at 202 K for the LaFe11.6Si1.4 composition without post-annealing processing. (C) 2017 Elsevier B.V. All rights reserved. |
| 公开日期 | 2017-12-25 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/13882]  |
| 专题 | 2017专题 |
| 推荐引用方式 GB/T 7714 | Yan, Aru,Shao, Yanyan,Liu, Jian,et al. Direct formation of NaZn13-structure La(Fe,Si)(13) phase by directional solidification[J]. MATERIALS LETTERS,2017,193:34-37. |
| APA | Yan, Aru,Shao, Yanyan,Liu, Jian,&Zhang, Pengna.(2017).Direct formation of NaZn13-structure La(Fe,Si)(13) phase by directional solidification.MATERIALS LETTERS,193,34-37. |
| MLA | Yan, Aru,et al."Direct formation of NaZn13-structure La(Fe,Si)(13) phase by directional solidification".MATERIALS LETTERS 193(2017):34-37. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。