Structure and high temperature tribological behavior of TiAlN/nitride duplex treated coatings on Ti6Al4V

文献类型:期刊论文

作者Xue, Qunji; Niu, Ruili; Li, Jinlong; Wang, Yongxin; Chen, Jianmin
刊名SURFACE & COATINGS TECHNOLOGY
出版日期2017
卷号309页码:232-241
ISSN号0257-8972
英文摘要The duplex treatment of nitriding and TiAlN coatings was employed to improve the wear resistance of the Ti6Al4V alloy at higher temperature. Mechanical properties, microstructure and high temperature tribological behaviors were investigated by ball-on-disc wear test at elevated temperatures from 25 degrees C to 600 degrees C in atmosphere. The duplex treated sample exhibits a superior adhesion compared with only TiAlN coated sample due to a good load-carrying capacity. In addition, the duplex treated sample possesses excellent abrasion resistance at all temperatures. Particularly, the duplex treated sample has the lowest wear rate at 500 degrees C due to the formation of Al2O3 and TiO2. (C) 2016 Published by Elsevier B.V.
公开日期2017-12-25
源URL[http://ir.nimte.ac.cn/handle/174433/14029]  
专题2017专题
推荐引用方式
GB/T 7714
Xue, Qunji,Niu, Ruili,Li, Jinlong,et al. Structure and high temperature tribological behavior of TiAlN/nitride duplex treated coatings on Ti6Al4V[J]. SURFACE & COATINGS TECHNOLOGY,2017,309:232-241.
APA Xue, Qunji,Niu, Ruili,Li, Jinlong,Wang, Yongxin,&Chen, Jianmin.(2017).Structure and high temperature tribological behavior of TiAlN/nitride duplex treated coatings on Ti6Al4V.SURFACE & COATINGS TECHNOLOGY,309,232-241.
MLA Xue, Qunji,et al."Structure and high temperature tribological behavior of TiAlN/nitride duplex treated coatings on Ti6Al4V".SURFACE & COATINGS TECHNOLOGY 309(2017):232-241.

入库方式: OAI收割

来源:宁波材料技术与工程研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。