Two feasible approaches to enhance the wear behaviors of NiCrBSi coating in atmosphere and aqueous environments
文献类型：期刊论文
| 作者 | Zheng, Wenru; Wang, Yongxin; Li, Xiaogang; Ye, Yuwei; Wang, Chunting; Xiong, Wei |
| 刊名 | SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES
 |
| 出版日期 | 2017 |
| 卷号 | 5期号:3 |
| 关键词 | Water Lubrication Ni Laser Flame Microstructure Performance Improvement Resistance Friction Surface |
| 英文摘要 | NiCrBSi coating was deposited successfully on the surface of 316 stainless steel substrate by means of plasma spraying. The microstructures and mechanical property were analyzed by scanning electron microscopy, x-ray diffraction, and a Vickers hardness tester. The wear performances of the coatings sliding against the GCr15 ball under ambient air and water conditions were investigated, and two feasible approaches (tungsten carbide (WC)-doping and heat treatment) were used to improve the tribological performance. Results showed that the hardness of the NiCrBSi coating increased by 12.5% and 28.5% and the porosity decreased by 26.1% and 47.8%, respectively, after WC-doping and heat treatment. During dry friction, the friction coefficient and wear rate of the NiCrBSi coating were about 0.47 and 1.4 x 10(-5) mm(3) N-1 m(-1), respectively. These values were higher than those obtained on other coatings. In water conditions, all coatings showed a lower friction and wear rate than that in ambient air, which was as a result of the lubrication effect of water. Significantly, with WC-doping and heat treatment, the friction coefficients of both coatings were about 18.5% and 36.7%, respectively, lower than that of the NiCrBSi coating. Furthermore, the wear rates of both coatings were about 20% and 70%, respectively, lower than that of the NiCrBSi coating. |
| 学科主题 | Chemistry ; Materials Science |
| 语种 | 英语 |
| 公开日期 | 2018-12-04 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/17504]  |
| 专题 | 2017专题 |
| 推荐引用方式 GB/T 7714 | Zheng, Wenru,Wang, Yongxin,Li, Xiaogang,et al. Two feasible approaches to enhance the wear behaviors of NiCrBSi coating in atmosphere and aqueous environments[J]. SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES,2017,5(3). |
| APA | Zheng, Wenru,Wang, Yongxin,Li, Xiaogang,Ye, Yuwei,Wang, Chunting,&Xiong, Wei.(2017).Two feasible approaches to enhance the wear behaviors of NiCrBSi coating in atmosphere and aqueous environments.SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES,5(3). |
| MLA | Zheng, Wenru,et al."Two feasible approaches to enhance the wear behaviors of NiCrBSi coating in atmosphere and aqueous environments".SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES 5.3(2017). |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。