Influence of lithium hexafluorophosphate/ethylene carbonate/dimethyl carbonate electrolyte soaking on heat seal strength of polyamide 6/aluminum/cast-polypropylene laminates used as lithium-ion battery packaging
文献类型：期刊论文
| 作者 | Guo, Zhansheng; Fan, Yang; Du, Shiyu |
| 刊名 | JOURNAL OF PLASTIC FILM & SHEETING
 |
| 出版日期 | 2018 |
| 卷号 | 34期号:1页码:43399 |
| 关键词 | Low-density Polyethylene Aluminum Foil Corrosion Behavior Adhesion Films Polypropylene Temperature Sorption Layers Acids |
| 英文摘要 | The heat-seal strength of polymer-metal-polymer laminates, widely used in the packaging industry and more recently for pouch lithium-ion batteries, is a critical factor for the integrity of flexible package structures during service. The influences of lithium hexafluorophosphate/ethylene carbonate/dimethyl carbonate (LiPF6/EC/DMC) electrolyte soaking time and storage temperature on heat-seal strength were investigated through T-peel testing using a universal testing machine. Sealed multilayer laminates' heat-seal strength and their failure modes were measured for specimens sealed at various heat-sealing temperatures and dwell times before and after exposure to room temperature and 60? soaking conditions. The soaking condition significantly influences heat-seal strength, especially for the packages heat-sealed at low temperatures and short heat-sealing times. Higher storage temperature during electrolyte-soaking accelerates the heat-seal strength decrease. Failure modes are affected by the soaking conditions and become more complicated than the packages without soaking. The optimized heat-sealing processing window is obtained under a certain soaking condition. The electrolyte hydrogen ion concentration (pH) decreases with longer soaking time and higher storage temperature, indicating that acidification may also contribute to decreased heat-seal strength. The results are important for understanding how stored lithium-ion batteries deteriorate and can help to guide battery design to maximize their shelf life. |
| 学科主题 | Energy & Fuels |
| 语种 | 英语 |
| 公开日期 | 2018-12-04 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/16943]  |
| 专题 | 2018专题 |
| 推荐引用方式 GB/T 7714 | Guo, Zhansheng,Fan, Yang,Du, Shiyu. Influence of lithium hexafluorophosphate/ethylene carbonate/dimethyl carbonate electrolyte soaking on heat seal strength of polyamide 6/aluminum/cast-polypropylene laminates used as lithium-ion battery packaging[J]. JOURNAL OF PLASTIC FILM & SHEETING,2018,34(1):43399. |
| APA | Guo, Zhansheng,Fan, Yang,&Du, Shiyu.(2018).Influence of lithium hexafluorophosphate/ethylene carbonate/dimethyl carbonate electrolyte soaking on heat seal strength of polyamide 6/aluminum/cast-polypropylene laminates used as lithium-ion battery packaging.JOURNAL OF PLASTIC FILM & SHEETING,34(1),43399. |
| MLA | Guo, Zhansheng,et al."Influence of lithium hexafluorophosphate/ethylene carbonate/dimethyl carbonate electrolyte soaking on heat seal strength of polyamide 6/aluminum/cast-polypropylene laminates used as lithium-ion battery packaging".JOURNAL OF PLASTIC FILM & SHEETING 34.1(2018):43399. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。