Melamine cyanurate tailored by base and its multi effects on flame retardancy of polyamide 6
文献类型：期刊论文
| 作者 | Tao, Wei; Li, Juan |
| 刊名 | APPLIED SURFACE SCIENCE
 |
| 出版日期 | 2018 |
| 卷号 | 456页码:751-762 |
| 关键词 | Fiber-reinforced Polyamide-6 Composite Lattice |
| 英文摘要 | In this paper, nitrogenous bases adenine (A), guanine (G), cytosine (C), and uracil (U), were used to tailor the hydrogen-bonded network of melamine cyanurate (MCA) and were noted as A-MCA, G-MCA, C-MCA, U-MCA, respectively. The results showed that the size, morphology and thermal behavior of MCA are regulated by base due to the formation of hydrogen bonds between them. These modified MCAs were used to improve the flame retardancy of polyamide 6 (PA6) which was evaluated by using the limiting oxygen index (LOI) and the vertical burning (UL-94) test, etc. The results showed that the PA6 sample containing 9 wt% C-MCA achieves the UL94 V-0 rating and has a LOI value of 30.7%, while the other samples with equal amounts of MCA only pass the UL-94 V-2 rating. The flame retardant mechanism was studied, and the results reveal that C-MCA with smaller size has greater contact area with PA6 which helps to catalyze the decomposition of PA6; Thus the PA6/C-MCA releases more NH3, CO2 etc., and produces more droplets than others, which dilutes combustible gas and takes away heat to make the samples extinguish. |
| 学科主题 | Materials Science |
| 语种 | 英语 |
| 公开日期 | 2018-12-04 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/17098]  |
| 专题 | 2018专题 |
| 推荐引用方式 GB/T 7714 | Tao, Wei,Li, Juan. Melamine cyanurate tailored by base and its multi effects on flame retardancy of polyamide 6[J]. APPLIED SURFACE SCIENCE,2018,456:751-762. |
| APA | Tao, Wei,&Li, Juan.(2018).Melamine cyanurate tailored by base and its multi effects on flame retardancy of polyamide 6.APPLIED SURFACE SCIENCE,456,751-762. |
| MLA | Tao, Wei,et al."Melamine cyanurate tailored by base and its multi effects on flame retardancy of polyamide 6".APPLIED SURFACE SCIENCE 456(2018):751-762. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。